LEXAN™ Copolymer 923X
聚碳酸酯
产品说明:
LEXAN923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 923x resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
添加剂 | |
特性 | Chlorine Free,冲击改性,可加工性，良好,快的成型周期,流动性高,无溴,延展性,阻燃性
|
用途 | |
外观 | |
加工方法 | |
Also Available In | |
密度 / 比重 | 1.19 |
| ASTM D792 |
熔流率（熔体流动速率） (300°C/1.2 kg) | 16 | g/10 min | ASTM D1238 |
收缩率 - 流动 (0.126 in) | 4.0E-3 到 8.0E-3 | in/in | 内部方法 |
拉伸模量 3 | 305000 | psi | ASTM D638 |
抗张强度 4 |
|
| ASTM D638 |
屈服 | 8410 | psi |
|
断裂 | 8700 | psi |
|
伸长率 4 |
|
| ASTM D638 |
屈服 | 6.0 | % |
|
断裂 | 110 | % |
|
弯曲模量 5 (1.97 in 跨距) | 348000 | psi | ASTM D790 |
弯曲强度 5 (屈服, 1.97 in 跨距) | 13100 | psi | ASTM D790 |
悬壁梁缺口冲击强度 |
|
| ASTM D256 |
-22°F | 12 | ft·lb/in |
|
73°F | 15 | ft·lb/in |
|
装有测量仪表的落镖冲击 (73°F, Total Energy) | 575 | in·lb | ASTM D3763 |
载荷下热变形温度 (264 psi, 未退火, 0.126 in) | 253 | °F | ASTM D648 |
维卡软化温度 | 284 | °F | ASTM D1525 6 |
线形热膨胀系数 |
|
| ASTM E831 |
流动 : -40 到 104°F | 3.4E-5 | in/in/°F |
|
横向 : -40 到 104°F | 3.4E-5 | in/in/°F |
|
RTI Elec | 257 | °F | UL 746 |
RTI Imp | 239 | °F | UL 746 |
RTI | 248 | °F | UL 746 |
UL 阻燃等级 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.12 in | 5VA |
|
|
灼热丝易燃指数 (0.06 in) | 1760 | °F | IEC 60695-2-12 |
热灯丝点火温度 |
|
| IEC 60695-2-13 |
0.06 in | 1520 | °F |
|
0.12 in | 1520 | °F |
|
干燥温度 | 248 | °F |
|
干燥时间 | 3.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
建议注射量 | 40 到 60 | % |
|
料筒后部温度 | 518 到 563 | °F |
|
料筒中部温度 | 536 到 581 | °F |
|
料筒前部温度 | 563 到 599 | °F |
|
射嘴温度 | 554 到 590 | °F |
|
加工（熔体）温度 | 563 到 599 | °F |
|
模具温度 | 158 到 203 | °F |
|
背压 | 43.5 到 102 | psi |
|
螺杆转速 | 40 到 70 | rpm |
|
排气孔深度 | 9.8E-4 到 3.0E-3 | in |
|
如需沙伯基础（SABIC）原厂物性表及相关文件，请联系我们工作人员，谢谢！