LEXAN™ Copolymer 4795R
聚碳酸酯
产品说明:
LEXAN 4795R is a high heat resistant poly(ester)carbonate injection molding resin. Flame Retardant.
特性 | |
用途 | |
加工方法 | |
Also Available In | |
密度 / 比重 |
|
|
|
-- | 1.20 |
| ASTM D792 |
-- | 1.20 | g/cm³ | ISO 1183 |
熔流率（熔体流动速率） (330°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
收缩率 |
|
| 内部方法 |
流动 : 0.126 in | 9.7E-3 | in/in |
|
横向流动 : 0.126 in | 9.7E-3 | in/in |
|
拉伸模量 2 | 315000 | psi | ASTM D638 |
抗张强度 3 |
|
| ASTM D638 |
屈服 | 9860 | psi |
|
断裂 | 10200 | psi |
|
伸长率 3 |
|
| ASTM D638 |
屈服 | 7.5 | % |
|
断裂 | 120 | % |
|
弯曲模量 4 (1.97 in 跨距) | 319000 | psi | ASTM D790 |
弯曲强度 4 (断裂, 1.97 in 跨距) | 15200 | psi | ASTM D790 |
悬壁梁缺口冲击强度 (73°F) | 11 | ft·lb/in | ASTM D256 |
无缺口悬臂梁冲击 (73°F) | 40 | ft·lb/in | ASTM D4812 |
装有测量仪表的落镖冲击 |
|
| ASTM D3763 |
73°F, Energy at Peak | 646 | in·lb |
|
73°F, Total Energy | 682 | in·lb |
|
载荷下热变形温度 |
|
| ASTM D648 |
66 psi, 未退火, 0.126 in | 320 | °F |
|
264 psi, 未退火, 0.126 in | 297 | °F |
|
维卡软化温度 | 327 | °F | ASTM D1525 5 |
Ball Pressure Test (253 到 261°F) | 通过 |
| IEC 60695-10-2 |
干燥温度 | 248 | °F |
|
干燥时间 | 3.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
建议注射量 | 40 到 60 | % |
|
料筒后部温度 | 617 到 662 | °F |
|
料筒中部温度 | 644 到 680 | °F |
|
料筒前部温度 | 662 到 698 | °F |
|
射嘴温度 | 653 到 689 | °F |
|
加工（熔体）温度 | 662 到 698 | °F |
|
模具温度 | 176 到 239 | °F |
|
背压 | 43.5 到 102 | psi |
|
螺杆转速 | 40 到 70 | rpm |
|
排气孔深度 | 9.8E-4 到 3.0E-3 | in |
|
如需沙伯基础（SABIC）原厂物性表及相关文件，请联系我们工作人员，谢谢！