Makrolon® Rx2635
聚碳酸酯
产品说明:
MVR (300 °C/1.2 kg) 12 cm³/10 min; medical devices; suitable for sterilization with high-energy radiation; biocompatible according to many ISO 10993-1 test requirements; medium viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in color code 451118 only; transparent parts for medical devices
密度 (73°F) | 1.20 | g/cm³ | ISO 1183 |
表观密度 2 | 0.66 | g/cm³ | ISO 60 |
熔流率（熔体流动速率） (300°C/1.2 kg) | 13 | g/10 min | ISO 1133 |
熔融体积流量（MVR） (300°C/1.2 kg) | 0.732 | in³/10min | ISO 1133 |
收缩率 |
|
| ISO 2577 |
横向流量 | 0.60 到 0.80 | % |
|
流量 | 0.60 到 0.80 | % |
|
吸水率 |
|
| ISO 62 |
饱和, 73°F | 0.30 | % |
|
平衡, 73°F, 50% RH | 0.12 | % |
|
拉伸模量 (73°F) | 348000 | psi | ISO 527-2/1 |
拉伸应力 |
|
| ISO 527-2/50 |
屈服, 73°F | 9720 | psi |
|
断裂, 73°F | 10900 | psi |
|
拉伸应变 |
|
| ISO 527-2/50 |
屈服, 73°F | 6.1 | % |
|
断裂, 73°F | 130 | % |
|
标称拉伸断裂应变 (73°F) | > 50 | % | ISO 527-2/50 |
简支梁无缺口冲击强度 |
|
| ISO 179/1eU |
-76°F | 无断裂 |
|
|
-22°F | 无断裂 |
|
|
73°F | 无断裂 |
|
|
悬壁梁缺口冲击强度 3 |
|
| ISO 7391 |
-22°F, 完全断裂 | 5.7 | ft·lb/in² |
|
73°F, 局部断裂 | 31 | ft·lb/in² |
|
多轴向仪器化冲击能量 (73°F) | 44.3 | ft·lb | ISO 6603-2 |
多轴向仪器化冲击力峰值 (73°F) | 1190 | lbf | ISO 6603-2 |
热变形温度 |
|
|
|
66 psi, 未退火 | 271 | °F | ISO 75-2/B |
264 psi, 未退火 | 250 | °F | ISO 75-2/A |
维卡软化温度 | 289 | °F | ISO 306/B50 |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 : 73 到 131°F | 3.6E-5 | in/in/°F |
|
横向 : 73 到 131°F | 3.6E-5 | in/in/°F |
|
表面电阻率 | 1.0E+16 | ohms | IEC 60093 |
体积电阻率 (73°F) | 1.0E+16 | ohms·cm | IEC 60093 |
Flash Ignition Temperature | 896 | °F | ASTM D1929 |
Self Ignition Temperature | 1022 | °F | ASTM D1929 |
ISO Shortname | ISO 7391-PC,MR,(,,)-18-9 |
|
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！