Bayblend® M303 FR
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
(PC+ABS)-Blend; Vicat/B 120 temperature = 115°C; suitable for use in electrical and electronic devices; Manufactured according to GMP; tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; for questions regarding biocompatibility we ask for an email inquiry under plastics@covestro.com
添加剂 | |
特性 | |
用途 | |
机构评级 | - ISO 10993 Part 10，ISO 10993 Part 5
|
RoHS 合规性 | |
密度 (73°F) | 1.19 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (260°C/5.0 kg) | 0.671 | in³/10min | ISO 1133 |
收缩率 |
|
| ISO 2577 |
横向流量 | 0.50 到 0.70 | % |
|
流量 | 0.50 到 0.70 | % |
|
吸水率 (饱和, 73°F) | 0.50 | % | ISO 62 |
拉伸模量 (73°F) | 384000 | psi | ISO 527-2/1 |
拉伸应力 |
|
| ISO 527-2/50 |
屈服, 73°F | 10000 | psi |
|
断裂, 73°F | 7690 | psi |
|
拉伸应变 (屈服, 73°F) | 5.0 | % | ISO 527-2/50 |
标称拉伸断裂应变 (73°F) | > 50 | % | ISO 527-2/50 |
悬壁梁缺口冲击强度 |
|
| ISO 180/A |
-22°F | 4.8 | ft·lb/in² |
|
73°F | 19 | ft·lb/in² |
|
无缺口伊佐德冲击强度 (73°F) | 无断裂 |
| ISO 180 |
热变形温度 |
|
|
|
66 psi, 未退火 | 223 | °F | ISO 75-2/B |
264 psi, 未退火 | 208 | °F | ISO 75-2/A |
维卡软化温度 |
|
|
|
-- | 235 | °F | ISO 306/B50 |
-- | 239 | °F | ISO 306/B120 |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 : 73 到 131°F | 3.8E-5 | in/in/°F |
|
横向 : 73 到 131°F | 4.0E-5 | in/in/°F |
|
表面电阻率 | 1.0E+17 | ohms | IEC 60093 |
体积电阻率 (73°F) | 1.0E+17 | ohms·cm | IEC 60093 |
介电强度 (73°F, 0.0394 in) | 890 | V/mil | IEC 60243-1 |
相对电容率 |
|
| IEC 60250 |
73°F, 100 Hz | 3.20 |
|
|
73°F, 1 MHz | 3.10 |
|
|
耗散因数 |
|
| IEC 60250 |
73°F, 100 Hz | 3.7E-3 |
|
|
73°F, 1 MHz | 7.5E-3 |
|
|
UL 阻燃等级 |
|
| UL 94 |
0.030 in, Internal Test | V-2 |
|
|
0.06 in, Internal Test | V-0 |
|
|
Melt Viscosity 2 (500°F) | 410 | Pa·s | ISO 11443-A |
ISO Shortname | PC+ABS-FR(40) |
|
|
如需科思创原厂物性表及相关文件，请联系我们工作人员，谢谢！