Zytel® ST811HS NC010

Zytel® ST811HS NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: NYLON 6/PA6
Product No: Zytel ST811HS NC010
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized

Zytel® ST811HS NC010

NYLON RESIN
Product Description:
Super Toughened, Heat Stabilized, Polyamide 6
Additive 
  • Heat Stabilizer，Mold Release 
Features 

  • Heat Stabilized

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 
  • ExtrusionInjection Molding 
Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Specific Volume vs Temperature (ISO 11403-2)

  • Tensile Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

  • PA6-HI

Resin ID (ISO 1043)

  • PA6-HI

Physical
Dry
Conditioned
Unit
Test Method
Density
1.04
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
1.4
--
%

Flow
0.90
--
%

Water Absorption



ISO 62
Saturation, 73°F, 0.0787 in
6.8
--
%

Equilibrium, 73°F, 0.0787 in, 50% RH
2.3
--
%

Hardness
Dry
Conditioned
Unit
Test Method
Rockwell Hardness (M-Scale)
60
--

ISO 2039-2
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus
131000
58000
psi
ISO 527-2
Tensile Stress (Yield)
4500
--
psi
ISO 527-2
Tensile Strain (Yield)
29
--
%
ISO 527-2
Nominal Tensile Strain at Break
> 50
--
%
ISO 527-2
Flexural Modulus
123000
52200
psi
ISO 178
Poisson's Ratio
0.45
0.47

ISO 527
Films
Dry
Conditioned
Unit
Test Method
Tensile Elongation - MD (Yield)
4.0
--
%
ISO 527-3
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
6.7
6.2
ft·lb/in²

73°F
34
61
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
No Break
No Break


73°F
No Break
No Break


Multi-Axial Instrumented Impact Energy



ISO 6603-2
-22°F
18.4
--
ft·lb

73°F
11.8
--
ft·lb

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
117
--
°F
ISO 75-2/A
Glass Transition Temperature 3
122
32.0
°F
ISO 11357-2
Vicat Softening Temperature
203
--
°F
ISO 306/B50
Melting Temperature 3
424
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.1E-4
--
in/in/°F

Transverse
1.0E-4
--
in/in/°F

Electrical
Dry
Conditioned
Unit
Test Method
Surface Resistivity
--
1.0E+15
ohms
IEC 60093
Volume Resistivity
1.0E+15
1.0E+13
ohms·cm
IEC 60093
Electric Strength
790
--
V/mil
IEC 60243-1
Dissipation Factor



IEC 60250
100 Hz
8.0E-3
0.055


1 MHz
0.014
0.18


Flammability
Dry
Conditioned
Unit
Test Method
Burning Rate 4 (0.0394 in)
< 3.9
--
in/min
ISO 3795
Flame Rating



UL 94, IEC 60695-11-10, -20
0.030 in
HB
--


0.06 in
HB
--


FMVSS Flammability
B
--

FMVSS 302
Fill Analysis
Dry
Conditioned
Unit

Melt Density
0.880
--
g/cm³

Ejection Temperature
374
--
°F

Specific Heat Capacity of Melt
0.621
--
Btu/lb/°F

Thermal Conductivity of Melt
1.0
--
Btu·in/hr/ft²/°F

Injection
Dry
Unit

Drying Temperature
140
°F

Drying Time - Desiccant Dryer
2.0 to 4.0
hr

Suggested Max Moisture
0.20
%

Processing (Melt) Temp
500 to 536
°F

Melt Temperature, Optimum
518
°F

Mold Temperature
122 to 194
°F

Mold Temperature, Optimum
158
°F

Holding Pressure
7250 to 14500
psi

Drying Recommended
yes


Hold Pressure Time
4.00
s/mm

Maximum Screw Tangential Speed
709
in/min