Zytel® BM73G15P BK317

Zytel® BM73G15P BK317

Manufacturer: Celanese
Produced At: Import/ China
Product Category: NYLON 6/PA6
Product No: Zytel® BM73G15P BK317
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized

Zytel® BM73G15P BK317

NYLON RESIN

Product Description:
15% Glass Reinforced Polyamide 6 Developed for Blow Molding
Filler / Reinforcement 

  • Glass Fiber, 15% Filler by Weight

Additive 

  • Heat Stabilizer，Lubricant，Mold Release

Features 

  • Heat Stabilized

Uses 

  • Blow Molding Applications

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Blow MoldingInjection Molding 

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Tensile Modulus vs. Temperature, Dynamic (ISO 11403-1)

Part Marking Code (ISO 11469)

  • PA6-IGF15

Resin ID (ISO 1043)

  • PA6-IGF15

Physical
Dry
Conditioned
Unit
Test Method
Density
1.22
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
0.60
--
%

Flow
0.40
--
%

Hardness
Dry
Conditioned
Unit
Test Method
Ball Indentation Hardness (H 961/30)
26100
--
psi
ISO 2039-1
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus
798000
377000
psi
ISO 527-2
Tensile Stress (Break)
16000
10200
psi
ISO 527-2
Tensile Strain (Break)
5.0
18
%
ISO 527-2
Flexural Modulus
725000
348000
psi
ISO 178
Poisson's Ratio
0.35
0.38

ISO 527
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength(73°F)
6.7
11
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength(73°F)
38
52
ft·lb/in²
ISO 179/1eU
Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed 2
419
--
°F
ISO 75-2/B
264 psi, Unannealed
374
--
°F
ISO 75-2/A
Glass Transition Temperature 3
140
--
°F
ISO 11357-2
Melting Temperature 3
428
--
°F
ISO 11357-3
Flammability
Dry
Conditioned
Unit
Test Method
Burning Rate 4 (0.0394 in)
1.5
--
in/min
ISO 3795
FMVSS Flammability
B
--

FMVSS 302
Fill Analysis
Dry
Conditioned
Unit
Test Method
Melt Viscosity (536°F, 1000 sec^-1)
350000
--
mPa·s
ISO 11443
Ejection Temperature
410
--
°F

Injection
Dry
Unit

Drying Temperature
176
°F

Drying Time - Desiccant Dryer
2.0 to 4.0
hr

Suggested Max Moisture
0.20
%

Processing (Melt) Temp
500 to 536
°F

Melt Temperature, Optimum
518
°F

Mold Temperature
158 to 248
°F

Mold Temperature, Optimum
212
°F

Holding Pressure
7250 to 14500
psi

Drying Recommended
yes


Hold Pressure Time
3.00
s/mm

Maximum Screw Tangential Speed
472
in/min

Extrusion
Dry
Unit

Drying Temperature
167 to 176
°F

Drying Time
4.0 to 6.0
hr

Suggested Max Moisture
0.050
%

Melt Temperature
455 to 482
°F

Extrusion Melt Temperature, Optimum
464
°F


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields