Products

Zytel® 73G30L NC010

Zytel® 73G30L NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: NYLON 6/PA6
Product No: Zytel 73G30L NC010
Product Quantity: 25KG / BAG

Zytel® 73G30L NC010

NYLON RESIN
Product Description:
30% Glass Reinforced Polyamide 6
Filler / Reinforcement 

  • Glass Fiber, 30% Filler by Weight

Additive 
  • Lubricant，Mold Release 
RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Creep Modulus vs. Time (ISO 11403-1)

  • Isochronous Stress vs. Strain (ISO 11403-1)

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

Part Marking Code (ISO 11469)

  • PA6-GF30

Resin ID (ISO 1043)

  • PA6-GF30

Physical
Dry
Conditioned
Unit
Test Method
Density
1.36
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
0.60
--
%

Flow
0.20
--
%

Water Absorption



ISO 62
Saturation, 73°F, 0.0787 in
6.3
--
%

Equilibrium, 73°F, 0.0787 in, 50% RH
1.9
--
%

Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus
1.45E+6
870000
psi
ISO 527-2
Tensile Stress (Break)
26100
17400
psi
ISO 527-2
Tensile Strain (Break)
3.5
6.0
%
ISO 527-2
Tensile Creep Modulus



ISO 899-1
1 hr
--
798000
psi

1000 hr
--
653000
psi

Flexural Modulus
1.23E+6
798000
psi
ISO 178
Flexural Stress
34800
--
psi
ISO 178
Compressive Stress
23200
--
psi
ISO 604
Shear Strength
8700
--
psi
ASTM D732
Poisson's Ratio
0.34
0.35

ISO 527
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-40°F
5.2
--
ft·lb/in²

-22°F
5.2
10
ft·lb/in²

73°F
6.7
11
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
38
38
ft·lb/in²

73°F
43
48
ft·lb/in²

Notched Izod Impact Strength



ISO 180/1A
-40°F
5.2
--
ft·lb/in²

-22°F
5.2
5.2
ft·lb/in²

73°F
7.1
9.5
ft·lb/in²

Unnotched Izod Impact Strength



ISO 180/1U
-22°F
43
--
ft·lb/in²

73°F
48
--
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
428
--
°F
ISO 75-2/B
264 psi, Unannealed
410
--
°F
ISO 75-2/A
Glass Transition Temperature 3
140
--
°F
ISO 11357-2
Melting Temperature 3
430
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
7.8E-6
--
in/in/°F

Transverse
5.7E-5
--
in/in/°F

Electrical
Dry
Conditioned
Unit
Test Method
Volume Resistivity
1.0E+14
--
ohms·cm
IEC 60093
Relative Permittivity (100 Hz)
3.80
--

IEC 60250
Dissipation Factor (100 Hz)
0.022
--

IEC 60250
Comparative Tracking Index (CTI)
PLC 0
--

UL 746
Comparative Tracking Index
600
--
V
IEC 60112
Flammability
Dry
Conditioned
Unit
Test Method
Burning Rate 4 (0.0394 in)
0.98
--
in/min
ISO 3795
Flame Rating



UL 94, IEC 60695-11-10, -20
0.06 in
HB
--


0.12 in
HB
--


Oxygen Index
21
--
%
ISO 4589-2
FMVSS Flammability
B
--

FMVSS 302
Fogging



ISO 6452
F-value (refraction)
95
--
%

G-value (condensate)
1.0E-4
--
g

Additional Information
Dry
Conditioned
Unit
Test Method
Emission of Organic Compounds
8.50
--
µgC/g
VDA 277
Odor
3.50
--

VDA 270
Injection
Dry
Unit

Drying Temperature
176
°F

Drying Time - Desiccant Dryer
2.0 to 4.0
hr

Suggested Max Moisture
0.20
%

Processing (Melt) Temp
500 to 536
°F

Melt Temperature, Optimum
518
°F

Mold Temperature
158 to 248
°F

Mold Temperature, Optimum
212
°F

Holding Pressure
7250 to 14500
psi

Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields