Zytel® HTN 53G50HSLR NC010
HIGH PERFORMANCE POLYAMIDE RESIN
Product Description:
50% Glass Reinforced High Performance Polyamide with Improved Impact and Stiffness
Filler / Reinforcement | |
Additive | |
Features | |
RoHS Compliance | |
Processing Method | |
Multi-Point Data | |
Part Marking Code (ISO 11469) | |
Part Marking Code (SAE J1344) | |
Resin ID (ISO 1043) | |
Density | 1.59 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage |
|
|
| ISO 294-4 |
Across Flow | 0.40 | -- | % |
|
Flow | 0.20 | -- | % |
|
Tensile Modulus | 2.39E+6 | 2.36E+6 | psi | ISO 527-2 |
Tensile Stress (Break) | 36300 | 31200 | psi | ISO 527-2 |
Tensile Strain (Break) | 2.8 | 3.2 | % | ISO 527-2 |
Flexural Modulus | 2.18E+6 | -- | psi | ISO 178 |
Poisson's Ratio | 0.33 | 0.33 |
| ISO 527 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-40°F | 6.7 | -- | ft·lb/in² |
|
73°F | 7.1 | -- | ft·lb/in² |
|
Charpy Unnotched Impact Strength(73°F) | 45 | -- | ft·lb/in² | ISO 179/1eU |
Notched Izod Impact Strength |
|
|
| ISO 180/1A |
-40°F | 6.4 | -- | ft·lb/in² |
|
73°F | 7.1 | -- | ft·lb/in² |
|
Heat Deflection Temperature (264 psi, Unannealed) | 457 | -- | °F | ISO 75-2/A |
Melting Temperature 3 | 500 | -- | °F | ISO 11357-3 |
CLTE |
|
|
| ISO 11359-2 |
Flow | 7.8E-6 | -- | in/in/°F |
|
Flow : -40 to 73°F | 9.4E-6 | -- | in/in/°F |
|
Transverse | 3.1E-5 | -- | in/in/°F |
|
Transverse : -40 to 73°F | 3.1E-5 | -- | in/in/°F |
|
Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
Comparative Tracking Index | 600 | -- | V | IEC 60112 |
Burning Rate 4 (0.0394 in) | 0.98 | -- | in/min | ISO 3795 |
Flame Rating |
|
|
| UL 94, IEC 60695-11-10, -20 |
0.030 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
Oxygen Index | 27 | -- | % | ISO 4589-2 |
FMVSS Flammability | B | -- |
| FMVSS 302 |
Drying Temperature | 212 | °F |
|
Drying Time - Desiccant Dryer | 6.0 to 8.0 | hr |
|
Suggested Max Moisture | 0.10 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Melt Temperature, Optimum | 554 | °F |
|
Mold Temperature | 194 to 230 | °F |
|
Drying Recommended | yes |
|
|