Products

vDelrin® 300TE BK602

vDelrin® 300TE BK602

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: POM
Product No: Delrin 300TE BK602
Product Quantity: 25KG / BAG
Product Features: Homopolymer，Low Emissions，Medium-high Viscosity

Delrin® 300TE BK602

ACETAL RESIN
Product Description:
Toughened Medium-high Viscosity Acetal Homopolymer with Very Low Emissions
Additive 
  • Lubricant,Mold Release 
Features 
  • Homopolymer,Low Emissions,Medium-high Viscosity
RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 
  • ExtrusionInjection MoldingProfile ExtrusionSheet Extrusion 
Multi-Point Data 
  • Shear Stress vs. Shear Rate (ISO 11403-1)Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)

  • POM-I

Resin ID (ISO 1043)

  • POM-I

Physical
Nominal Value
Unit
Test Method
Density
1.37
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)
6.0
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
0.262
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
1.5
%

Flow
1.3
%

Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness


ISO 2039-2
M-Scale
69


R-Scale
116


Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
305000
psi
ISO 527-2
Tensile Stress (Yield)
7980
psi
ISO 527-2
Tensile Strain (Yield)
20
%
ISO 527-2
Nominal Tensile Strain at Break
25
%
ISO 527-2
Flexural Modulus
290000
psi
ISO 178
Flexural Stress (3.5% Strain)
7980
psi
ISO 178
Poisson's Ratio
0.40

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
3.8
ft·lb/in²

73°F
7.1
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
71
ft·lb/in²

73°F
No Break


Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
277
°F
ISO 75-2/B
264 psi, Unannealed
172
°F
ISO 75-2/A
CLTE


ISO 11359-2
Flow
6.1E-5
in/in/°F

Transverse
6.7E-5
in/in/°F

Annealing Temperature
320
°F

Annealing Time - Optional
30.0
min/mm

Flammability
Nominal Value
Unit
Test Method
Burning Rate 2 (0.0394 in)
< 3.9
in/min
ISO 3795
FMVSS Flammability
B

FMVSS 302
Fill Analysis
Nominal Value
Unit
Test Method
Melt Density
1.15
g/cm³

Additional Information
Nominal Value
Unit
Test Method
Emission
< 2.00
mg/kg
VDA 275
Injection
Nominal Value
Unit

Drying Temperature
176
°F

Drying Time - Desiccant Dryer
4.0 to 8.0
hr

Suggested Max Moisture
0.050
%

Processing (Melt) Temp
392 to 410
°F

Melt Temperature, Optimum
401
°F

Mold Temperature
104 to 140
°F

Mold Temperature, Optimum
122
°F

Holding Pressure
8700 to 11600
psi

Drying Recommended
yes


Hold Pressure Time
7.50
s/mm

Extrusion
Nominal Value
Unit

Drying Temperature
167 to 185
°F

Drying Time
2.0 to 4.0
hr

Suggested Max Moisture
0.050
%

Melt Temperature
383 to 401
°F

Extrusion Melt Temperature, Optimum
392
°F


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields