Products

Delrin® 127UV NC010

Delrin® 127UV NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: POM
Product No: Delrin 127UV NC010
Product Quantity: 25KG / BAG
Product Features: High Viscosity，Homopolymer，UV Stabilized

Delrin® 127UV NC010

ACETAL RESIN
Product Description:
UV Stabilized High Viscosity Acetal Homopolymer
Additive 
  • Lubricant，Mold Release，UV Stabilizer
Features 
  • High Viscosity，Homopolymer，UV Stabilized
RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 
  • Extrusion，Injection Molding，Profile Extrusion，Sheet Extrusion 
Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Specific Volume vs Temperature (ISO 11403-2)

  • Tensile Modulus vs. Temperature (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

  • POM

Resin ID (ISO 1043)

  • POM

Physical
Nominal Value
Unit
Test Method
Density
1.42
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)
2.4
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
0.116
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
1.9
%

Flow
2.1
%

Water Absorption


ISO 62
73°F, 24 hr
0.50
%

Saturation, 73°F, 0.0787 in
1.2
%

Equilibrium, 73°F, 0.0787 in, 50% RH
0.30
%

Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness


ISO 2039-2
M-Scale
92


R-Scale
120


Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
435000
psi
ISO 527-2
Tensile Stress (Yield)
10200
psi
ISO 527-2
Tensile Strain (Yield)
23
%
ISO 527-2
Nominal Tensile Strain at Break
45
%
ISO 527-2
Flexural Modulus
377000
psi
ISO 178
Flexural Stress


ISO 178
--
10400
psi

3.5% Strain
11700
psi

Poisson's Ratio
0.37

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
5.2
ft·lb/in²

73°F
7.1
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
170
ft·lb/in²

73°F
190
ft·lb/in²

Notched Izod Impact Strength


ISO 180/1A
-40°F
5.2
ft·lb/in²

73°F
6.2
ft·lb/in²

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
320
°F
ISO 75-2/B
264 psi, Unannealed
199
°F
ISO 75-2/A
Vicat Softening Temperature
320
°F
ISO 306/B50
Melting Temperature 3
352
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
6.7E-5
in/in/°F

Transverse
6.1E-5
in/in/°F

Annealing Temperature
320
°F

Annealing Time - Optional
30.0
min/mm

Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
1.0E+13
ohms·cm
IEC 60093
Relative Permittivity


IEC 60250
100 Hz
3.50


1 MHz
3.40


Comparative Tracking Index
600
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Burning Rate 4 (0.0394 in)
1.1
in/min
ISO 3795
Flame Rating



0.031 in
HB

UL 94
0.03 in
HB

IEC 60695-11-10, -20
FMVSS Flammability
B

FMVSS 302
Additional Information
Nominal Value
Unit
Test Method
Emission
< 8.00
mg/kg
VDA 275
Injection
Nominal Value
Unit

Drying Temperature
176
°F

Drying Time - Desiccant Dryer
2.0 to 4.0
hr

Suggested Max Moisture
0.20
%

Processing (Melt) Temp
410 to 428
°F

Melt Temperature, Optimum
419
°F

Mold Temperature
176 to 212
°F

Mold Temperature, Optimum
194
°F

Holding Pressure
13100 to 16000
psi

Drying Recommended
yes


Hold Pressure Time
8.00
s/mm

Extrusion
Nominal Value
Unit

Drying Temperature
167 to 185
°F

Drying Time
2.0 to 4.0
hr

Suggested Max Moisture
0.20
%

Melt Temperature
383 to 401
°F

Extrusion Melt Temperature, Optimum
392
°F


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields