Products

Delrin® 100ST BK602

Delrin® 100ST BK602

Manufacturer: Delrin
Produced At: Import/ China
Product Category: POM
Product No: Delrin® 100ST BK602
Product Quantity: 25KG / BAG
Product Features: High Viscosity，Homopolymer

Delrin® 100ST BK602

ACETAL RESIN

Product Description:
Super Toughened High Viscosity Acetal Homopolymer
Additive 

  • Lubricant，Mold Release 

Features 

  • High Viscosity，Homopolymer 

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Extrusion，Injection Molding，Profile Extrusion，Sheet Extrusion 

Multi-Point Data 

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

Part Marking Code (ISO 11469)

  • POM-HI

Resin ID (ISO 1043)

  • POM-HI

Physical
Nominal Value
Unit
Test Method
Density
1.33
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)
2.1
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
0.110
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
1.1
%

Flow
0.80
%

Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
203000
psi
ISO 527-2
Tensile Stress (Yield)
5800
psi
ISO 527-2
Tensile Strain (Yield)
30
%
ISO 527-2
Nominal Tensile Strain at Break
> 50
%
ISO 527-2
Flexural Modulus
160000
psi
ISO 178
Poisson's Ratio
0.43

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
6.7
ft·lb/in²

73°F
38
ft·lb/in²

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
216
°F
ISO 75-2/B
264 psi, Unannealed
140
°F
ISO 75-2/A
Melting Temperature 3
352
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
6.7E-5
in/in/°F

Transverse
6.7E-5
in/in/°F

Annealing Temperature
320
°F

Annealing Time - Optional
30.0
min/mm

Flammability
Nominal Value
Unit
Test Method
Burning Rate 4 (0.0394 in)
1.6
in/min
ISO 3795
Flame Rating (0.06 in)
HB

UL 94, IEC 60695-11-10, -20
FMVSS Flammability
B

FMVSS 302
Additional Information
Nominal Value
Unit
Test Method
Emission
< 8.00
mg/kg
VDA 275
Injection
Nominal Value
Unit

Drying Temperature
176
°F

Drying Time - Desiccant Dryer
4.0 to 8.0
hr

Suggested Max Moisture
0.050
%

Processing (Melt) Temp
392 to 410
°F

Melt Temperature, Optimum
401
°F

Mold Temperature
104 to 140
°F

Mold Temperature, Optimum
122
°F

Holding Pressure
8700 to 11600
psi

Drying Recommended
yes


Hold Pressure Time
7.50
s/mm

Extrusion
Nominal Value
Unit

Drying Temperature
167 to 185
°F

Drying Time
2.0 to 4.0
hr

Suggested Max Moisture
0.050
%

Melt Temperature
383 to 401
°F

Extrusion Melt Temperature, Optimum
392
°F


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields