Products

Delrin® 100 NC010

Delrin® 100 NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: POM
Product No: Delrin 100 NC010
Product Quantity: 25KG / BAG
Product Features: High Viscosity，Homopolymer

Delrin® 100 NC010

ACETAL RESIN
Product Description:
High Viscosity Acetal Homopolymer
Additive 

  • Mold Release

Features 

  • High Viscosity,Homopolymer 

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Extrusion,Injection Molding,Profile Extrusion,Sheet Extrusion 

Multi-Point Data 

  • Coefficient of Thermal Expansion vs. Temperature (ISO 11403-1)

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Specific Volume vs Temperature (ISO 11403-2)

  • Tensile Modulus vs. Temperature (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

  • POM

Resin ID (ISO 1043)

  • POM

Physical
Nominal Value
Unit
Test Method
Density
1.42
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)
2.3
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
0.116
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
1.9
%

Flow
2.2
%

Water Absorption


ISO 62
Saturation, 73°F, 0.0787 in
0.90
%

Equilibrium, 73°F, 0.0787 in, 50% RH
0.20
%

Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness


ISO 2039-2
M-Scale
90


R-Scale
121


Ball Indentation Hardness (H 358/30)
25100
psi
ISO 2039-1
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
421000
psi
ISO 527-2
Tensile Stress (Yield)
10300
psi
ISO 527-2
Tensile Strain (Yield)
26
%
ISO 527-2
Nominal Tensile Strain at Break
45
%
ISO 527-2
Tensile Creep Modulus


ISO 899-1
1 hr
421000
psi

1000 hr
232000
psi

Flexural Modulus
399000
psi
ISO 178
Flexural Stress


ISO 178
--
13500
psi

3.5% Strain
11500
psi

Compressive Stress
16000
psi
ISO 604
Poisson's Ratio
0.37

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
6.2
ft·lb/in²

73°F
6.7
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
200
ft·lb/in²

73°F
No Break


Notched Izod Impact Strength


ISO 180/1A
-40°F
6.2
ft·lb/in²

73°F
6.7
ft·lb/in²

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
320
°F
ISO 75-2/B
264 psi, Unannealed
203
°F
ISO 75-2/A
Vicat Softening Temperature



--
347
°F
ISO 306/A50
--
320
°F
ISO 306/B50
Melting Temperature 3
352
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
6.1E-5
in/in/°F

Flow : -40 to 73°F
5.6E-5
in/in/°F

Transverse
6.1E-5
in/in/°F

Transverse : -40 to 73°F
5.6E-5
in/in/°F

Annealing Temperature
320
°F

Annealing Time - Optional
30.0
min/mm

Effective Thermal Diffusivity
1.00E-7
m²/s

Temperature Index


IEC 60216
Tensile Strength, 20000 hr
230
°F

Tensile Strength, 5000 hr
257
°F

Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
3.0E+13
ohms
IEC 60093
Volume Resistivity
> 1.0E+15
ohms·cm
IEC 60093
Electric Strength
1000
V/mil
IEC 60243-1
Relative Permittivity


IEC 60250
100 Hz
3.90


1 MHz
3.80


Dissipation Factor


IEC 60250
100 Hz
1.0E-3


1 MHz
5.5E-3


Comparative Tracking Index
600
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Burning Rate 4 (0.0394 in)
1.2
in/min
ISO 3795
Flame Rating



0.031 in
HB

UL 94
0.06 in
HB

UL 94, IEC 60695-11-10, -20
0.03 in
HB

IEC 60695-11-10, -20
FMVSS Flammability
B

FMVSS 302
Fogging - G-value (condensate)
3.0E-4
g
ISO 6452
Fill Analysis
Nominal Value
Unit
Test Method
Melt Density
1.19
g/cm³

Specific Heat Capacity of Melt
0.717
Btu/lb/°F

Additional Information
Nominal Value
Unit
Test Method
Emission
< 8.00
mg/kg
VDA 275

如需杜邦（DUPONT）原厂物性表及相关文件，请联系我们工作人员，谢谢！

Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields


Consultation