Amodel® ET-1000 HS

Amodel® ET-1000 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel ET-1000 HS
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant,Ductile,Heat Stabilized,Hot Water Moldability,Impact Modified,Low Warpag

Amodel® ET-1000 HS

Polyphthalamide
Product Description:
Amodel® ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel® PPA resins, ET-1000 HS offers high fatigue strength, good chemical resistance and high mechanical property retention over a broad temperature and humidity range.

  • Natural: ET-1000 HS NT

Additive 
  • Heat Stabilizer,Impact Modifier 
Features 
  • Chemical Resistant,Ductile,Heat Stabilized,Hot Water Moldability,Impact Modified,Low Warpage
Uses 
  • Automotive Applications,,Automotive Electronics,Automotive Under the Hood,Connectors,General Purpose,Housings,Industrial Applications,Industrial Parts,Lawn and Garden Equipment,Machine/Mechanical Parts,Metal Replacement
RoHS Compliance 

  • RoHS Compliant

Appearance 

  • Natural Color

Forms 

  • Pellets

Processing Method 

  • Water-Heated Mold Injection Molding

Physical
Dry
Conditioned
Unit
Test Method
Density
1.13
--
g/cm³
ISO 1183/A
Molding Shrinkage



ASTM D955
Flow
0.015
--
in/in

Across Flow
0.015
--
in/in

Water Absorption (24 hr)
0.70
--
%
ASTM D570
Hardness
Dry
Conditioned
Unit
Test Method
Rockwell Hardness (R-Scale)
120
--

ASTM D785
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus




--
350000
350000
psi
ASTM D638
73°F
350000
--
psi
ISO 527-2
212°F
290000
--
psi
ISO 527-2
Tensile Stress




Yield, 73°F
10200
--
psi
ISO 527-2
Yield, 212°F
4900
--
psi
ISO 527-2
Break, 73°F
8700
--
psi
ISO 527-2
-40°F
16000
14000
psi
ASTM D638
73°F
10000
9100
psi
ASTM D638
Tensile Elongation




Yield, -40°F
9.0
9.0
%
ASTM D638
Yield, 73°F
6.0
6.0
%
ASTM D638
Yield, 73°F
5.0
--
%
ISO 527-2
Yield, 212°F
4.3
--
%
ISO 527-2
Break, -40°F
12
11
%
ASTM D638
Break, 73°F
20
18
%
ASTM D638
Break, 73°F
7.0
--
%
ISO 527-2
Break, 212°F
95
--
%
ISO 527-2
Flexural Modulus




--
330000
310000
psi
ASTM D790
73°F
260000
--
psi
ISO 178
212°F
190000
--
psi
ISO 178
Flexural Strength




--
15800
12400
psi
ASTM D790
73°F
10200
--
psi
ISO 178
212°F
6400
--
psi
ISO 178
Shear Strength
8500
--
psi
ASTM D732
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)
6.00
--
mg
ASTM D1044
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength(73°F)
37
--
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength(73°F)
No Break
--

ISO 179/1eU
Notched Izod Impact




-40°F
2.0
--
ft·lb/in
ASTM D256
73°F
17
20
ft·lb/in
ASTM D256
73°F
35
--
ft·lb/in²
ISO 180/1A
Unnotched Izod Impact Strength(73°F)
No Break
--

ISO 180/1U
Instrumented Dart Impact



ASTM D3763
Energy to Maximum Load 3
336
--
in·lb

Total Energy
480
--
in·lb

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




264 psi, Unannealed
228
--
°F
ISO 75-2/A
264 psi, Annealed
248
--
°F
ASTM D648
Melting Temperature
590
--
°F
ISO 11357-3, ASTM D3418
CLTE



ASTM E831
Flow : 32 to 212°F
4.3E-5
--
in/in/°F

Flow : 212 to 392°F
7.8E-5
--
in/in/°F

Transverse : 32 to 212°F
4.5E-5
--
in/in/°F

Transverse : 212 to 392°F
6.1E-5
--
in/in/°F

Injection
Dry
Unit

Drying Temperature
230
°F

Drying Time
4.0
hr

Suggested Max Moisture
0.030 to 0.060
%

Rear Temperature
580 to 605
°F

Front Temperature
600 to 625
°F

Processing (Melt) Temp
610 to 650
°F

Mold Temperature
> 275
°F

Injection Notes
MOLD TEMPERATURE

  • If the wall is thick, lower temperatures may be used to prevent ejector pin problems.


STORAGE:

  • Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields