Products

Amodel® AT-6130 HS

Amodel® AT-6130 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AT-6130 HS
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant,Good Flow,Heat Stabilized,High Heat Resistance,High Strength,Hot Water Moldability,Impact Modified,Low Friction,Lubricated,Wear Resistant

Amodel® AT-6130 HS
Polyphthalamide
Product Description:
Amodel® AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel® resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. The processing window is relatively broad and mold temperatures as low as 150°F (65°C) can be used.

  • Black: AT-6130 HS BK 324

  • Natural: AT-6130 HS NT

Filler / Reinforcement 

  • Glass Fiber, 30% Filler by Weight

Additive 
  • Heat Stabilizer,Impact Modifier,Lubricant,Mold Release 
Features 
  • Chemical Resistant,Good Flow,Heat Stabilized,High Heat Resistance,High Strength,Hot Water Moldability,Impact Modified,Low Friction,Lubricated,Wear Resistant
Uses 
  • Automotive Applications,Automotive Electronics,Automotive Under the Hood,Bearings,Connectors,Fuel Lines,General Purpose,Housings,Industrial Applications,Industrial Parts,Lawn and Garden Equipment,Machine/Mechanical Parts,Metal Replacement,Valves/Valve Parts
RoHS Compliance 

  • RoHS Compliant

Appearance 
  • Black,Natural Color 
Forms 

  • Pellets

Processing Method 

  • Water-Heated Mold Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

Physical
Dry
Conditioned
Unit
Test Method
Density
1.34
--
g/cm³
ISO 1183/A
Molding Shrinkage



ASTM D955
Flow
5.0E-3
--
in/in

Across Flow
8.0E-3
--
in/in

Water Absorption (24 hr)
0.15
--
%
ASTM D570
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus
1.35E+6
--
psi
ISO 527-2
Tensile Strength




Break
24200
--
psi
ASTM D638
Break
24600
--
psi
ISO 527-2
Tensile Elongation




Break
3.2
--
%
ASTM D638
Break
3.3
--
%
ISO 527-2
Flexural Modulus




--
1.14E+6
--
psi
ASTM D790
--
1.10E+6
--
psi
ISO 178
Flexural Stress




--
32600
--
psi
ISO 178
Yield
34200
--
psi
ASTM D790
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength
6.0
--
ft·lb/in²
ISO 179/1eA
Notched Izod Impact
2.5
--
ft·lb/in
ASTM D256
Unnotched Izod Impact
26
--
ft·lb/in
ASTM D256
Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
568
--
°F
ISO 75-2/B
264 psi, Unannealed
529
--
°F
ISO 75-2/A
Melting Temperature




--
590
--
°F
ISO 11357-3
--
583
--
°F
ASTM D3418
Injection
Dry
Unit

Drying Temperature
250
°F

Drying Time
4.0
hr

Suggested Max Moisture
0.030 to 0.060
%

Rear Temperature
600 to 615
°F

Front Temperature
620 to 630
°F

Processing (Melt) Temp
610 to 635
°F

Mold Temperature
150 to 200
°F

Injection Rate
Fast


Injection Notes
Injection pressure between 2-4 in/sec (5-10 cm/sec). Adjust the holding pressure to one-half the injection pressure.

Storage:

  • Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields


Consultation