Products

Amodel® AT-1116 HS

Amodel® AT-1116 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AT-1116 HS
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant，Good Dimensional Stability，Heat Stabilized，High Heat Resistance，Impact Modified

Amodel® AT-1116 HS

Polyphthalamide
Product Description:
Amodel® AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass reinforced PPA.

Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly.

  • Black: AT-1116 HS BK 324

  • Natural: AT-1116 HS NT

Filler / Reinforcement 

  • Glass Fiber, 16% Filler by Weight

Additive 
  • Heat Stabilizer,Impact Modifier 
Features 
  • Chemical Resistant,Good Dimensional Stability,Heat Stabilized,High Heat Resistance,Impact Modified
Uses 

  • Automotive Applications,Automotive Electronics,Automotive Under the HoodBearings,Bobbins,Connectors,General Purpose,

  • Industrial Applications,Industrial Parts,

  • Machine/Mechanical Parts,Metal Replacement

RoHS Compliance 

  • RoHS Compliant

Appearance 
  • Black,Natural Color 
Forms 

  • Pellets

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1) 

Physical
Dry
Conditioned
Unit
Test Method
Density
1.28
--
g/cm³
ISO 1183/A
Molding Shrinkage



ASTM D955
Flow
6.0E-3
--
in/in

Across Flow
6.0E-3
--
in/in

Water Absorption (24 hr)
0.20
--
%
ASTM D570
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus




--
940000
1.03E+6
psi
ASTM D638
73°F
1.00E+6
--
psi
ISO 527-2
212°F
970000
--
psi
ISO 527-2
Tensile Stress




Break, 73°F
23200
--
psi
ISO 527-2
Break, 212°F
9500
--
psi
ISO 527-2
--
23300
19000
psi
ASTM D638
Tensile Elongation




Break
3.8
2.8
%
ASTM D638
Break, 73°F
3.7
--
%
ISO 527-2
Break, 212°F
4.2
--
%
ISO 527-2
Flexural Modulus




--
870000
900000
psi
ASTM D790
73°F
970000
--
psi
ISO 178
212°F
720000
--
psi
ISO 178
Flexural Strength




--
32800
29100
psi
ASTM D790
73°F
28600
--
psi
ISO 178
212°F
20500
--
psi
ISO 178
Compressive Strength
18000
--
psi
ASTM D695
Shear Strength
10100
9500
psi
ASTM D732
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength(73°F)
4.3
--
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength(73°F)
41
--
ft·lb/in²
ISO 179/1eU
Notched Izod Impact




--
1.8
0.90
ft·lb/in
ASTM D256
73°F
3.8
--
ft·lb/in²
ISO 180/1A
Unnotched Izod Impact




--
18
15
ft·lb/in
ASTM D256
73°F
25
--
ft·lb/in²
ISO 180/1U
Instrumented Dart Impact



ASTM D3763
Energy at Maxumum Load 3
--
12.0
in·lb

Energy at Maxumum Load 4
15.6
--
in·lb

Total Energy
88.8
67.2
in·lb

Thermal
Dry
Conditioned
Unit
Test Method
Deflection Temperature Under Load




66 psi, Annealed
515
--
°F
ASTM D648
264 psi, Unannealed
497
--
°F
ISO 75-2/A
264 psi, Annealed
489
--
°F
ASTM D648
Peak Melting Temperature
590
--
°F
ASTM D3418
CLTE



ASTM E831
Flow : 32 to 212°F
1.2E-5
--
in/in/°F

Flow : 212 to 392°F
8.9E-6
--
in/in/°F

Transverse : 32 to 212°F
4.2E-5
--
in/in/°F

Transverse : 212 to 392°F
6.7E-5
--
in/in/°F

Injection
Dry
Unit

Drying Temperature
230
°F

Drying Time
4.0
hr

Suggested Max Moisture
0.030 to 0.060
%

Rear Temperature
580 to 605
°F

Front Temperature
600 to 625
°F

Processing (Melt) Temp
610 to 650
°F

Mold Temperature
275
°F

Injection Notes
Storage:

  • Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields