Amodel® AS-1933 HS

Amodel® AS-1933 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AS-1933 HS
Product Quantity: 25KG / BAG
Product Features: Antifreeze Resistant，Chemical Resistant，Creep Resistant，Good Dimensional Stability，Good Glycol Resistance，Good，Stiffness，Heat Stabilized，High Heat Resistance，High Strength

Amodel® AS-1933 HS

Polyphthalamide
Product Description:
Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C).

Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves.

  • Black: AS-1933 HS BK 324

Filler / Reinforcement 

  • Glass Fiber, 33% Filler by Weight

Additive 

  • Heat Stabilizer

Features 
  • Antifreeze Resistant,Chemical Resistant,Creep Resistant,Good Dimensional Stability,Good Glycol Resistance,Good Stiffness,Heat Stabilized,High Heat Resistance,High Strength
Uses 
  • Automotive Applications,Automotive Under the Hood,Housings,Industrial Applications,Industrial Parts,Machine/Mechanical Parts,Metal Replacement,Power/Other Tools,Thick-walled Parts,Valves/Valve Parts
RoHS Compliance 

  • RoHS Compliant

Appearance 

  • Black

Forms 

  • Pellets

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1) 

Physical
Nominal Value
Unit
Test Method
Density
1.45
g/cm³
ISO 1183/A
Molding Shrinkage


ASTM D955
Flow
2.0E-3
in/in

Across Flow
6.0E-3
in/in

Water Absorption (24 hr)
0.21
%
ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus



--
1.70E+6
psi
ASTM D638
-- 3
1.10E+6
psi
ASTM D638
--
1.83E+6
psi
ISO 527-2
Tensile Strength



Break
32000
psi
ASTM D638
Break 3
11000
psi
ASTM D638
Break
30700
psi
ISO 527-2
Tensile Elongation (Break)
2.5
%
ASTM D638, ISO 527-2
Flexural Modulus



--
1.56E+6
psi
ASTM D790
--
1.54E+6
psi
ISO 178
Flexural Stress



--
44800
psi
ISO 178
Yield
45400
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength
4.8
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength
36
ft·lb/in²
ISO 179/1eU
Notched Izod Impact



--
1.7
ft·lb/in
ASTM D256
-- 3
1.0
ft·lb/in
ASTM D256
--
4.5
ft·lb/in²
ISO 180/1A
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load



264 psi, Unannealed
530
°F
ASTM D648
264 psi, Unannealed
532
°F
ISO 75-2/Af
Melting Temperature
594
°F
ISO 11357-3
Injection
Nominal Value
Unit

Drying Temperature
250
°F

Drying Time
4.0
hr

Suggested Max Moisture
0.030 to 0.060
%

Hopper Temperature
175
°F

Rear Temperature
580 to 605
°F

Front Temperature
600 to 625
°F

Processing (Melt) Temp
610 to 650
°F

Mold Temperature
275
°F

Injection Notes
Storage:

  • Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.