Amodel® A-4160 HSL

Amodel® A-4160 HSL

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel A-4160 HSL
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant，Creep Resistant，Fast Molding Cycle，Good Dimensional Stability，Good Toughness，Heat Stabilized，High Heat Resistance，High Strength，Hot Water Moldability，Low CLTE，Lubricated，Ultra High Stiffness

Amodel® A-4160 HSL

Polyphthalamide
Product Description:
Amodel® A-4160 HSL resin is a 60% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits high modulus at elevated temperatures, a high heat deflection temperature and exceptional creep resistance. This material was designed for metal replacement applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity.

  • Black: A-4160 HSL BK324

Filler / Reinforcement 

  • Glass Fiber, 60% Filler by Weight

Additive 
  • Heat Stabilizer，Lubricant，Mold Release
Features 
  • Chemical Resistant，Creep Resistant，Fast Molding Cycle，Good Dimensional Stability，Good ToughnessHeat Stabilized，High Heat Resistance，High Strength，Hot Water Moldability，Low CLTELubricated，Ultra High Stiffness
Uses 
  • Automotive Applications，Automotive Electronics，Automotive Under the Hood，Camera Applications，Cell Phones，Connectors，Electrical/Electronic Applications，Housings，Industrial Applications，Machine/Mechanical Parts，Metal Replacement，Transmission Applications
RoHS Compliance 

  • RoHS Compliant

Appearance 

  • Black

Forms 

  • Pellets

Processing Method 

  • Water-Heated Mold Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

Physical
Nominal Value
Unit
Test Method
Density
1.75
g/cm³
ISO 1183/A
Molding Shrinkage


ISO 294-4
Across Flow
0.80
%

Flow
0.50
%

Water Absorption (73°F, 24 hr)
0.19
%
ISO 62
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus


ISO 527-2
73°F
3.38E+6
psi

392°F
1.27E+6
psi

Tensile Stress


ISO 527-2
Break, 73°F
35400
psi

Break, 392°F
11500
psi

Tensile Strain


ISO 527-2
Break, 73°F
1.4
%

Break, 392°F
3.3
%

Flexural Modulus


ISO 178
73°F
2.80E+6
psi

392°F
1.23E+6
psi

Flexural Stress


ISO 178
73°F
55800
psi

392°F
19900
psi

Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (73°F)
6.0
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength (73°F)
61
ft·lb/in²
ISO 179/1eU
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
579
°F
ISO 75-2/A
Injection
Nominal Value
Unit

Drying Temperature
248
°F

Drying Time
4.0
hr

Rear Temperature
605 to 615
°F

Front Temperature
620 to 630
°F

Processing (Melt) Temp
625 to 650
°F

Mold Temperature
150 to 200
°F

Injection Notes
Injection Pressure: 3 to 4 in/sec

Storage:

  • Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields