CYCOLAC™ Resin FR15U

CYCOLAC™ Resin FR15U

Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate
Product No: CYCOLAC Resin FR15U
Product Quantity: 25KG / BAG
Product Features: Flame Retardant，Good Moldability，UV Resistant

CYCOLAC™ Resin FR15U

Acrylonitrile Butadiene Styrene
Product Description:
Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94V-0/5VA rated. Elevated UL RTI rating.
Features 
  • Flame Retardant,Good Moldability,UV Resistant
Processing Method 

  • Injection Molding

Multi-Point Data 

  • Coefficient of Thermal Expansion vs. Temperature (ASTM E831)

  • Flexural DMA (ASTM D4065)

  • Shear DMA (ASTM D4065)

  • Specific Heat vs. Temperature (ASTM D3417)

  • Tensile Fatigue

  • Tensile Stress vs. Strain (ASTM D638)

  • Thermal Conductivity vs. Temperature (ASTM E1530)

  • Viscosity vs. Shear Rate (ASTM D3835)

Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity



--
1.19

ASTM D792
--
1.19
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)



230°C/3.8 kg
3.3
g/10 min
ASTM D1238
220°C/5.0 kg
7.0
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
2.44
in³/10min
ISO 1133
Molding Shrinkage - Flow (0.126 in)
5.0E-3 to 7.0E-3
in/in
Internal Method
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus



-- 3
300000
psi
ASTM D638
--
321000
psi
ISO 527-2/1
Tensile Strength



Yield 4
5500
psi
ASTM D638
Yield
5960
psi
ISO 527-2/50
Break 4
4400
psi
ASTM D638
Tensile Elongation



Yield 4
2.4
%
ASTM D638
Break 4
17
%
ASTM D638
Break
22
%
ISO 527-2/50
Flexural Modulus



1.97 in Span 5
340000
psi
ASTM D790
-- 6
328000
psi
ISO 178
Flexural Stress



-- 6, 7
9180
psi
ISO 178
Yield, 1.97 in Span 5
9800
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact



73°F
4.0
ft·lb/in
ASTM D256
73°F 8
5.7
ft·lb/in²
ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
252
in·lb
ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load


ASTM D648
66 psi, Unannealed, 0.126 in
187
°F

264 psi, Unannealed, 0.126 in
167
°F

Vicat Softening Temperature



--
201
°F
ASTM D1525 9
--
198
°F
ISO 306/B50
CLTE


ASTM E831
Flow : -40 to 104°F
5.0E-5
in/in/°F

Transverse : -40 to 104°F
5.1E-5
in/in/°F

RTI Elec
194
°F
UL 746
RTI Imp
185
°F
UL 746
RTI Str
194
°F
UL 746
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
> 1.0E+14
ohms·cm
IEC 60093
Electric Strength (0.126 in, in Oil)
510
V/mil
IEC 60243-1
Arc Resistance 10
PLC 7

ASTM D495
Comparative Tracking Index (CTI)
PLC 1

UL 746
High Amp Arc Ignition (HAI)
PLC 4

UL 746
High Voltage Arc Tracking Rate (HVTR)
PLC 4

UL 746
Hot-wire Ignition (HWI)
PLC 2

UL 746
Flammability
Nominal Value
Unit
Test Method
Flame Rating


UL 94
0.06 in
V-0


0.11 in
5VA


Fill Analysis
Nominal Value
Unit
Test Method
Melt Viscosity (392°F, 1000 sec^-1)
320
Pa·s
ASTM D3835
Injection
Nominal Value
Unit

Drying Temperature
180 to 190
°F

Drying Time
2.0 to 4.0
hr

Drying Time, Maximum
8.0
hr

Suggested Max Moisture
0.10
%

Suggested Shot Size
50 to 70
%

Rear Temperature
340 to 360
°F

Middle Temperature
390 to 410
°F

Front Temperature
400 to 430
°F

Nozzle Temperature
400 to 450
°F

Processing (Melt) Temp
400 to 450
°F

Mold Temperature
120 to 160
°F

Back Pressure
50.0 to 100
psi

Screw Speed
30 to 60
rpm

Vent Depth
1.5E-3 to 2.0E-3
in


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields