CYCOLAC™ Resin FR15

CYCOLAC™ Resin FR15

Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate
Product No: CYCOLAC Resin FR15
Product Quantity: 25KG / BAG
Product Features: Flame Retardant，Good Moldability，Good Toughness

CYCOLAC™ Resin FR15

Acrylonitrile Butadiene Styrene
Product Description:
Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated.
Additive 

  • Flame Retardant

Features 
  • Flame Retardant,Good Moldability,Good Toughness
Processing Method 

  • Injection Molding

Multi-Point Data 

  • Coefficient of Thermal Expansion vs. Temperature (ASTM E831)

  • Flexural DMA (ASTM D4065)

  • Shear DMA (ASTM D4065)

  • Specific Heat vs. Temperature (ASTM D3417)

  • Tensile Fatigue

  • Tensile Stress vs. Strain (ASTM D638)

  • Thermal Conductivity vs. Temperature (ASTM E1530)

  • Viscosity vs. Shear Rate (ASTM D3835)

Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity



--
1.20

ASTM D792
--
1.19
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR)



230°C/3.8 kg
4.0
g/10 min
ASTM D1238
220°C/5.0 kg
10
g/10 min
ISO 1133
Molding Shrinkage - Flow (0.126 in)
5.0E-3 to 7.0E-3
in/in
Internal Method
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus 3
340000
psi
ASTM D638
Tensile Strength



Yield 4
6000
psi
ASTM D638
Yield
5980
psi
ISO 527-2/50
Break 4
5100
psi
ASTM D638
Break
4540
psi
ISO 527-2/50
Tensile Elongation



Yield 4
2.3
%
ASTM D638
Yield
2.1
%
ISO 527-2/50
Break 4
9.0
%
ASTM D638
Break
34
%
ISO 527-2/50
Flexural Modulus 5 (1.97 in Span)
395000
psi
ASTM D790
Flexural Strength 5 (Yield, 1.97 in Span)
10400
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 6 (73°F)
9.3
ft·lb/in²
ISO 179/1eA
Notched Izod Impact



73°F
4.0
ft·lb/in
ASTM D256
-22°F 7
3.1
ft·lb/in²
ISO 180/1A
73°F 7
8.9
ft·lb/in²
ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
300
in·lb
ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load



66 psi, Unannealed, 0.126 in
180
°F
ASTM D648
264 psi, Unannealed, 0.126 in
158
°F
ASTM D648
264 psi, Unannealed, 2.52 in Span 8
164
°F
ISO 75-2/Af
Vicat Softening Temperature



--
187
°F
ASTM D1525 9
--
178
°F
ISO 306/B50
--
183
°F
ISO 306/B120
CLTE


ASTM E831
Flow : -40 to 104°F
4.7E-5
in/in/°F

Transverse : -40 to 104°F
4.8E-5
in/in/°F

RTI Elec
140
°F
UL 746
RTI Imp
140
°F
UL 746
RTI Str
140
°F
UL 746
Electrical
Nominal Value

Test Method
Arc Resistance 10
PLC 7

ASTM D495
Comparative Tracking Index (CTI)
PLC 2

UL 746
High Amp Arc Ignition (HAI)
PLC 4

UL 746
High Voltage Arc Tracking Rate (HVTR)
PLC 4

UL 746
Hot-wire Ignition (HWI)
PLC 3

UL 746
Flammability
Nominal Value

Test Method
Flame Rating


UL 94
0.06 in
V-0


0.10 in
5VA


Fill Analysis
Nominal Value
Unit
Test Method
Melt Viscosity (392°F, 1000 sec^-1)
290
Pa·s
ASTM D3835
Injection
Nominal Value
Unit

Drying Temperature
180 to 190
°F

Drying Time
2.0 to 4.0
hr

Drying Time, Maximum
6.0
hr

Suggested Max Moisture
0.10
%

Suggested Shot Size
50 to 70
%

Rear Temperature
340 to 360
°F

Middle Temperature
380 to 400
°F

Front Temperature
390 to 420
°F

Nozzle Temperature
390 to 430
°F

Processing (Melt) Temp
390 to 430
°F

Mold Temperature
120 to 160
°F

Back Pressure
50.0 to 100
psi

Screw Speed
30 to 60
rpm

Vent Depth
1.5E-3 to 2.0E-3
in