CYCOLAC™ Resin EX58

CYCOLAC™ Resin EX58

Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate
Product No: CYCOLAC Resin EX58
Product Quantity: 25KG / BAG
Product Features: High Impact Resistance

CYCOLAC™ Resin EX58

Acrylonitrile Butadiene Styrene
Product Description:
High impact ABS for sheet extrusion and blow molding applications.
Features 

  • High Impact Resistance

Uses 

  • Blow Molding Applications Sheet 

Processing Method 

  • Extrusion Blow Molding Sheet Extrusion 

Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity



--
1.03

ASTM D792
--
1.03
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
4.0
g/10 min
ISO 1133
Molding Shrinkage - Flow (0.126 in)
6.0E-3 to 8.0E-3
in/in
Internal Method
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
102

ASTM D785
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus



-- 2
302000
psi
ASTM D638
--
286000
psi
ISO 527-2/1
Tensile Strength



Yield 3
5660
psi
ASTM D638
Yield
5950
psi
ISO 527-2/50
Break 3
4350
psi
ASTM D638
Break
4350
psi
ISO 527-2/50
Tensile Elongation



Yield 3
3.1
%
ASTM D638
Yield
2.6
%
ISO 527-2/50
Break 3
32
%
ASTM D638
Break
21
%
ISO 527-2/50
Flexural Modulus



1.97 in Span 4
313000
psi
ASTM D790
-- 5
290000
psi
ISO 178
Flexural Stress



-- 5, 6
8700
psi
ISO 178
Yield, 1.97 in Span 4
9570
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 7 (73°F)
18
ft·lb/in²
ISO 179/1eA
Notched Izod Impact



-22°F
5.6
ft·lb/in
ASTM D256
73°F
8.1
ft·lb/in
ASTM D256
-22°F 8
11
ft·lb/in²
ISO 180/1A
73°F 8
17
ft·lb/in²
ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
327
in·lb
ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load



66 psi, Unannealed, 0.126 in
196
°F
ASTM D648
264 psi, Unannealed, 0.126 in
169
°F
ASTM D648
264 psi, Unannealed, 2.52 in Span 9
172
°F
ISO 75-2/Af
Vicat Softening Temperature



--
223
°F
ASTM D1525 10
--
203
°F
ISO 306/B50
--
207
°F
ISO 306/B120
CLTE


ASTM E831
Flow : -40 to 104°F
5.6E-5
in/in/°F

Transverse : -40 to 104°F
5.8E-5
in/in/°F

RTI Elec
140
°F
UL 746
RTI Imp
140
°F
UL 746
RTI Str
140
°F
UL 746
Electrical
Nominal Value

Test Method
Arc Resistance 11
PLC 5

ASTM D495
Comparative Tracking Index (CTI)
PLC 0

UL 746
High Amp Arc Ignition (HAI)
PLC 4

UL 746
High Voltage Arc Tracking Rate (HVTR)
PLC 1

UL 746
Hot-wire Ignition (HWI)
PLC 4

UL 746
Flammability
Nominal Value

Test Method
Flame Rating (0.06 in)
HB

UL 94
Fill Analysis
Nominal Value
Unit
Test Method
Melt Viscosity (464°F, 100 sec^-1)
1550
Pa·s
ASTM D3835
Extrusion Notes
Extrusion Blow Molding Parameters:

  • Adapter - Zone 5 Temperature: 210 - 232 C

  • Barrel - Zone 1 Temperature: 204 - 227 C

  • Barrel - Zone 2 Temperature: 204 - 227 C

  • Barrel - Zone 3 Temperature: 204 - 227 C

  • Barrel - Zone 4 Temperature: 204 - 227 C

  • Die Temperature: 216 - 235 C

  • Drying Temperature: 82 - 88 C

  • Drying Time: 4 - 5 hrs

  • Drying Time (Cumulative): 24 hrs

  • Extruder Feed Zone Temperature: 60 - 77 C

  • Head - Zone 6 - Top Temperature: 216 - 232 C

  • Head - Zone 7 - Bottom Temperature: 216 - 232 C

  • Maximum Moisture Content: .02 %

  • Melt Temperature (Parison): 216 - 232 C

  • Mold Temperature: 38 - 82 C

  • Screw Speed: 20 - 60 rpm


Sheet Extrusion Parameters:

  • Adapter Temperature: 204 - 249 C

  • Barrel - Zone 1 Temperature: 171 - 199 C

  • Barrel - Zone 2 Temperature: 182 - 221 C

  • Barrel - Zone 3 Temperature: 188 - 227 C

  • Barrel - Zone 4 Temperature: 199 - 238 C

  • Die Temperature: 204 - 249 C

  • Drying Temperature: 82 - 93 C

  • Drying Time: 4 hrs

  • Maximum Moisture Content: .02 %

  • Melt Temperature: 216 - 260 C

  • Roll Stack Temp - Bottom: 99 - 104 C

  • Roll Stack Temp - Middle: 93 - 104 C

  • Roll Stack Temp - Top: 88 - 93 C