Arnite® AV2 340 XL

Arnite® AV2 340 XL

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyethylene Terephthalate（PET）
Product No: Arnite AV2 340 XL   
Product Quantity: 25KG / BAG
Product Features: Low to No Outgassing

Arnite® AV2 340 XL

Polyethylene Terephthalate
Product Description:
20% Glass Reinforced, Low Outgassing

Special Features:

  • Low outgassing


Used In:

  • Bezels and AFL Frames


Arnite® (PBT, PET and blends) are high-performance engineering plastics that combine high strength and rigidity with excellent processing characteristics. As a result, Arnite® A (PET) and Arnite® T (PBT) are well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
A wide portfolio of Arnite® is available including unreinforced, reinforced and flame retardant grades.
Filler / Reinforcement 

  • Glass Fiber, 20% Filler by Weight

Features 

  • Low to No Outgassing

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PET-GF20

Physical
Nominal Value
Unit
Test Method
Density
1.52
g/cm³
ISO 1183
Molding Shrinkage


ISO 294-4
Across Flow
1.1
%

Flow
0.40
%

Water Absorption


ISO 62
Saturation, 73°F
0.50
%

Equilibrium, 73°F, 50% RH
0.25
%

Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.15E+6
psi
ISO 527-2
Tensile Stress (Break)
21800
psi
ISO 527-2
Tensile Strain (Break)
2.9
%
ISO 527-2
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (73°F)
3.8
ft·lb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength (73°F)
19
ft·lb/in²
ISO 179/1eU
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
473
°F
ISO 75-2/B
264 psi, Unannealed
410
°F
ISO 75-2/A
Melting Temperature 2
491
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
1.7E-5
in/in/°F

Transverse
3.9E-5
in/in/°F

Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
> 1.0E+15
ohms·cm
IEC 60093
Flammability
Nominal Value
Unit
Test Method
Flammability Classification


IEC 60695-11-10, -20
0.031 in
HB


0.06 in
HB


Injection
Nominal Value
Unit

Drying Temperature
212 to 248
°F

Drying Time
3.0 to 12
hr

Rear Temperature
536 to 572
°F

Middle Temperature
554 to 590
°F

Front Temperature
554 to 590
°F

Nozzle Temperature
554 to 590
°F

Processing (Melt) Temp
554 to 590
°F

Mold Temperature
266 to 284
°F

Injection Rate
Moderate-Fast


Back Pressure
435 to 1450
psi

Screw Compression Ratio
2.5:1.0



Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields