Texin® 250
Thermoplastic Polyurethane Elastomer (Polyester)
Texin 250 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 50D. It is processed primarily by extrusion and blow molding but can also be used for injection molding.
Features | - Abrasion Resistant，Chemical Resistant，Low Gel，Medium Clarity，Oil Resistant，Solvent Resistant
|
Uses | - Film，Footwear，Hose，Profiles，Sheet，Tubing
|
Agency Ratings | - FDA 21 CFR 177.1680，FDA 21 CFR 177.2600
|
Appearance | |
Processing Method | - Blow Molding，Extrusion，Injection Molding
|
Density / Specific Gravity |
|
|
|
-- | 1.22 |
| ASTM D792 |
-- | 1.22 | g/cm³ | ISO 1183 |
Molding Shrinkage |
|
|
|
Flow : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
Across Flow : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
Across Flow : 0.100 in | 0.80 | % | ISO 2577 |
Flow : 0.100 in | 0.80 | % | ISO 2577 |
Durometer Hardness |
|
| ASTM D2240, ISO 868 |
Shore A | 95 |
|
|
Shore D | 50 |
|
|
Flexural Modulus |
|
| ASTM D790, ISO 178 |
73°F | 12000 | psi |
|
158°F | 5220 | psi |
|
Taber Abrasion Resistance |
|
|
|
1000 Cycles, 1000 g, H-18 Wheel | 70.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 Wheel | 70.0 | mg | ISO 4649 |
Tensile Stress |
|
| ASTM D412, ISO 37 |
100% Strain | 1700 | psi |
|
300% Strain | 4600 | psi |
|
Tensile Strength (Yield) | 6700 | psi | ASTM D412, ISO 37 |
Tensile Elongation (Break) | 400 | % | ASTM D412, ISO 37 |
Tear Strength |
|
|
|
-- 2 | 775 | lbf/in | ASTM D624 |
-- | 780 | lbf/in | ISO 34-1 |
Compression Set 3 |
|
| ASTM D395B, ISO 815 |
73°F, 22 hr | 15 | % |
|
158°F, 22 hr | 35 | % |
|
Bayshore Resilience | 25 | % | ASTM D2632 |
Glass Transition Temperature | -4.00 | °F | DMA |
Vicat Softening Temperature | 239 | °F | ISO 306/A50, ASTM D1525 4 |
Drying Temperature - Desiccant Dryer | 199 to 219 | °F |
|
Drying Time - Desiccant Dryer | 2.0 | hr |
|
Suggested Max Moisture | 0.030 | % |
|
Suggested Max Regrind | 20 | % |
|
Rear Temperature | 374 to 410 | °F |
|
Middle Temperature | 374 to 419 | °F |
|
Front Temperature | 392 to 428 | °F |
|
Nozzle Temperature | 401 to 437 | °F |
|
Processing (Melt) Temp | 401 to 419 | °F |
|
Mold Temperature | 59 to 104 | °F |
|
Injection Pressure | 6000 to 15000 | psi |
|
Injection Rate | Slow-Moderate |
|
|
Back Pressure | < 200 | psi |
|
Screw Speed | 40 to 80 | rpm |
|
Cushion | 0.125 | in |
|
Hold Pressure: 60 to 80% of Injection Pressure |
Drying Temperature | 199 to 219 | °F |
|
Drying Time | 2.0 | hr |
|
Suggested Max Regrind | 20 | % |
|
Cylinder Zone 1 Temp. | 356 to 392 | °F |
|
Cylinder Zone 3 Temp. | 356 to 401 | °F |
|
Cylinder Zone 5 Temp. | 356 to 410 | °F |
|
Melt Temperature | 374 to 401 | °F |
|
Die Temperature | 365 to 410 | °F |
|