Heraflex® E 7722 1000 NAT
Thermoplastic Copolyester Elastomer
TPC-ET Thermoplastic Elastomer. High Modulus, Nominal Shore D/15s 69. Natural colour
Features | |
RoHS Compliance | |
Appearance | |
Resin ID (ISO 1043) | |
Density | 1.25 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
Shore Hardness |
|
| ISO 868 |
Shore D, 3 sec | 77 |
|
|
Shore D, 15 sec | 69 |
|
|
Tensile Modulus | 196000 | psi | ISO 527-2/1A/1 |
Tensile Stress |
|
| ISO 527-2/1A/50 |
Yield | 6960 | psi |
|
Break | 4210 | psi |
|
10% Strain | 6530 | psi |
|
100% Strain | 4640 | psi |
|
Tensile Strain (Yield) | 15 | % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 350 | % | ISO 527-2/1A/50 |
Flexural Modulus 2 | 183000 | psi | ISO 178 |
Flexural Stress 2 | 7250 | psi | ISO 178 |
Abrasion Resistance | 39.0 | mm³ | ASTM D1004 |
Charpy Notched Impact Strength (73°F) | 4.8 | ft·lb/in² | ISO 179/1eA |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 239 | °F | ISO 75-2/Bf |
264 psi, Unannealed | 140 | °F | ISO 75-2/Af |
Vicat Softening Temperature | 410 | °F | ISO 306/B50 |
Melting Temperature 3 | 426 | °F | ISO 11357-3 |
Surface Resistivity 4 | 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity 4 | 1.0E+15 | ohms·cm | IEC 60093 |
Tear Strength | 1400 | lbf/in | DIN 53516 |
Drying Temperature - Desiccant Dryer | 230 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | < -22 | °F |
|
Suggested Max Moisture | 0.050 | % |
|
Processing (Melt) Temp | 464 to 482 | °F |
|
Mold Temperature | 86 to 122 | °F |
|
Injection Rate | Moderate |
|
|