RTP 3881

RTP 3881

Manufacturer: RTP Company
Produced At: Import / China
Product Category: Polyaryletherketone（PAEK）
Product No: RTP 3881
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant，Electrically Conductive，Good Moldability，Good Stiffness，Good Thermal Stability，High Strength

RTP 3881

Polyaryletherketone
Product Description:
Warning: The status of this material is 'Commercial: Limited Issue'

The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
Filler / Reinforcement 

  • Carbon Fiber, 10% Filler by Weight

Features 
  • Chemical Resistant,Electrically Conductive,Good Moldability,Good Stiffness,Good Thermal Stability,High Strength
RoHS Compliance 

  • Contact Manufacturer

Appearance 
  • Black,Natural Color 
Forms 

  • Pellets

Processing Method 

  • Injection Molding

Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity
1.33

ASTM D792
Molding Shrinkage - Flow
2.0E-3 to 3.0E-3
in/in
ASTM D955
Water Absorption (24 hr, 73°F)
0.20
%
ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.70E+6
psi
ASTM D638
Tensile Strength (Yield)
25100
psi
ASTM D638
Tensile Elongation (Break)
2.4
%
ASTM D638
Flexural Modulus
1.50E+6
psi
ASTM D790
Flexural Strength (Yield)
38400
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact (0.125 in)
1.0
ft·lb/in
ASTM D256
Unnotched Izod Impact (0.125 in)
10
ft·lb/in
ASTM D4812
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load (264 psi, Unannealed)
600
°F
ASTM D648
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
2.0E+3
ohms·cm
ASTM D257
Flammability
Nominal Value
Unit
Test Method
Flame Rating
V-0

UL 94
Injection
Nominal Value
Unit

Drying Temperature
300
°F

Drying Time
3.0
hr

Suggested Max Moisture
0.010
%

Suggested Max Regrind
20
%

Rear Temperature
675 to 750
°F

Middle Temperature
690 to 785
°F

Front Temperature
725 to 800
°F

Mold Temperature
300 to 425
°F

Injection Pressure
10000 to 18000
psi

Back Pressure
25.0 to 100
psi

Screw Speed
60 to 90
rpm

Clamp Tonnage
5.0 to 8.0
tons/in²
 
Filler / Reinforcement Carbon Fiber, 10% Filler by WeightFeatures Chemical ResistantElectrically ConductiveGood MoldabilityGood StiffnessGood Thermal StabilityHigh StrengthRoHS Compliance Contact ManufacturerAppearance BlackNatural Color Forms PelletsProcessing Method Injection Molding
PhysicalNominal ValueUnitTest MethodDensity / Specific Gravity1.33 ASTM D792Molding Shrinkage - Flow2.0E-3 to 3.0E-3in/inASTM D955Water Absorption (24 hr, 73°F)0.20%ASTM D570
MechanicalNominal ValueUnitTest MethodTensile Modulus1.70E+6psiASTM D638Tensile Strength (Yield)25100psiASTM D638Tensile Elongation (Break)2.4%ASTM D638Flexural Modulus1.50E+6psiASTM D790Flexural Strength (Yield)38400psiASTM D790ImpactNominal ValueUnitTest MethodNotched Izod Impact (0.125 in)1.0ft·lb/inASTM D256Unnotched Izod Impact (0.125 in)10ft·lb/inASTM D4812
ThermalNominal ValueUnitTest MethodDeflection Temperature Under Load (264 psi, Unannealed)600°FASTM D648
ElectricalNominal ValueUnitTest MethodVolume Resistivity2.0E+3ohms·cmASTM D257FlammabilityNominal ValueUnitTest MethodFlame RatingV-0 UL 94
InjectionNominal ValueUnit Drying Temperature300°F Drying Time3.0hr Suggested Max Moisture0.010% Suggested Max Regrind20% Rear Temperature675 to 750°F Middle Temperature690 to 785°F Front Temperature725 to 800°F Mold Temperature300 to 425°F Injection Pressure10000 to 18000psi Back Pressure25.0 to 100psi Screw Speed60 to 90rpm Clamp Tonnage5.0 to 8.0tons/in² 


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields


Consultation