TECHNYL STAR® AFX 216 V60 GREY 2327
Polyamide 66
Product Description:
TECHNYL STAR® AFX 216 V60 Grey 2327 is a high flow polyamide 66 resin, reinforced with 60% of glass fibre, for injection moulding. Due to its outstanding flow caracteristics, this grade shows exceptional processing behaviour and excellent surface aspect of the finished part.
Filler / Reinforcement | |
Features | - Good Dimensional Stability，High Flow，High Stiffness，Outstanding Surface Finish
|
Uses | - GearsWhite Goods & Small Appliances
|
Agency Ratings | |
Appearance | |
Forms | |
Processing Method | |
Multi-Point Data | |
Resin ID (ISO 1043) | |
Density | 1.71 | -- | g/cm³ | ISO 1183/A |
Molding Shrinkage |
|
|
| ISO 294-4 |
Across Flow | 0.45 | -- | % |
|
Flow | 0.35 | -- | % |
|
Water Absorption (73°F, 24 hr) | 0.52 | -- | % | ISO 62 |
Tensile Modulus |
|
|
|
|
73°F | 2.84E+6 | -- | psi | ASTM D638 |
73°F | 3.19E+6 | 2.39E+6 | psi | ISO 527-2/1A |
Tensile Strength |
|
|
|
|
Break, 73°F | 36300 | -- | psi | ASTM D638 |
Break, 73°F | 37700 | 28300 | psi | ISO 527-2/1A |
Tensile Elongation |
|
|
|
|
Yield, 73°F | 2.0 | -- | % | ASTM D638 |
Break, 73°F | 2.0 | -- | % | ASTM D638 |
Break, 73°F | 2.2 | 2.9 | % | ISO 527-2 |
Flexural Modulus |
|
|
|
|
73°F | 2.61E+6 | -- | psi | ASTM D790 |
73°F | 2.61E+6 | 1.91E+6 | psi | ISO 178 |
Flexural Strength |
|
|
|
|
73°F | 53700 | -- | psi | ASTM D790 |
73°F | 58000 | 43500 | psi | ISO 178 |
Charpy Notched Impact Strength(73°F) | 7.1 | 7.1 | ft·lb/in² | ISO 179/1eA |
Charpy Unnotched Impact Strength(73°F) | 43 | 41 | ft·lb/in² | ISO 179/1eU |
Notched Izod Impact (73°F) | 3.2 | -- | ft·lb/in | ASTM D256 |
Deflection Temperature Under Load |
|
|
|
|
264 psi, Unannealed | 487 | -- | °F | ASTM D648 |
264 psi, Unannealed | 496 | -- | °F | ISO 75-2/Af |
Melting Temperature | 504 | -- | °F | ISO 11357-3 |
Flame Rating |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.13 in | HB | -- |
|
|
Drying Temperature | 176 | °F |
|
Suggested Max Moisture | 0.20 | % |
|
Rear Temperature | 509 to 527 | °F |
|
Middle Temperature | 518 to 536 | °F |
|
Front Temperature | 536 to 554 | °F |
|
Mold Temperature | 140 to 194 | °F |
|
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4h Injection Advice: For reinforced polyamides, Solvay recommends the use of steel with a high content of carbon, and purified for polishing, to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). In the case of high requirements on surface quality a mould temperature of up to 120°C can be considered.
|