Rynite® 530 NC010

Rynite® 530 NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: PET
Product No: Rynite 530 NC010
Product Quantity: 25KG / BAG



Rynite® 530 NC010

THERMOPLASTIC POLYESTER RESIN
Product Description:
30% Glass Reinforced Polyethylene Terephthalate
Filler / Reinforcement 

  • Glass Fiber, 30% Filler by Weight

Additive 

  • Mold Release

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Creep Modulus vs. Time (ISO 11403-1)

  • Isochronous Stress vs. Strain (ISO 11403-1)

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

  • PET-GF30

Resin ID (ISO 1043)

  • PET-GF30

Physical
Nominal Value
Unit
Test Method
Density
1.56
g/cm³
ISO 1183
Melt Volume-Flow Rate (MVR) (280°C/2.16 kg)
0.305
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
0.80
%

Flow
0.20
%

Water Absorption


ISO 62
Saturation, 73°F, 0.0787 in
0.70
%

Equilibrium, 73°F, 0.0787 in, 50% RH
0.20
%

Viscosity Number
55.0
cm³/g
ISO 307
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness


ISO 2039-2
M-Scale
100


R-Scale
120


Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.60E+6
psi
ISO 527-2
Tensile Stress (Break)
22900
psi
ISO 527-2
Tensile Strain (Break)
2.5
%
ISO 527-2
Tensile Creep Modulus


ISO 899-1
1 hr
1.57E+6
psi

1000 hr
1.28E+6
psi

Flexural Modulus
1.30E+6
psi
ISO 178
Flexural Stress
33400
psi
ISO 178
Poisson's Ratio
0.34

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-40°F
4.8
ft·lb/in²

-22°F
5.2
ft·lb/in²

73°F
5.2
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
21
ft·lb/in²

73°F
29
ft·lb/in²

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
473
°F
ISO 75-2/B
264 psi, Unannealed
435
°F
ISO 75-2/A
Vicat Softening Temperature
446
°F
ISO 306/B50
Melting Temperature 3
486
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
5.6E-6
in/in/°F

Flow : -40 to 73°F
1.2E-5
in/in/°F

Flow : 131 to 320°F
2.2E-6
in/in/°F

Transverse
4.5E-5
in/in/°F

Transverse : -40 to 73°F
3.7E-5
in/in/°F

Transverse : 131 to 320°F
5.9E-5
in/in/°F

Thermal Conductivity
2.0
Btu·in/hr/ft²/°F

Effective Thermal Diffusivity
1.30E-7
m²/s

Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
1.0E+14
ohms
IEC 60093
Volume Resistivity
1.0E+15
ohms·cm
IEC 60093
Electric Strength
810
V/mil
IEC 60243-1
Relative Permittivity


IEC 60250
100 Hz
4.20


1 MHz
3.80


Dissipation Factor


IEC 60250
100 Hz
0.013


1 MHz
7.0E-3


Comparative Tracking Index (CTI)
PLC 2

UL 746
Comparative Tracking Index
250
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Burning Rate 4 (0.0394 in)
1.5
in/min
ISO 3795
Flame Rating


UL 94, IEC 60695-11-10, -20
0.030 in
HB


0.06 in
HB


Oxygen Index
20
%
ISO 4589-2
FMVSS Flammability
B

FMVSS 302
Fogging - G-value (condensate)
0.0
g
ISO 6452
Fill Analysis
Nominal Value
Unit
Test Method
Ejection Temperature
338
°F

Additional Information
Nominal Value
Unit
Test Method
Emission of Organic Compounds
16.0
µgC/g
VDA 277
Odor
3.00

VDA 270
Injection
Nominal Value
Unit

Drying Temperature
248
°F

Drying Time - Desiccant Dryer
4.0 to 6.0
hr

Suggested Max Moisture
0.020
%

Processing (Melt) Temp
536 to 572
°F

Melt Temperature, Optimum
545
°F

Mold Temperature
248 to 284
°F

Mold Temperature, Optimum
266
°F

Holding Pressure
11600
psi

Back Pressure
As low as possible


Drying Recommended
yes


Hold Pressure Time
4.00
s/mm

Maximum Screw Tangential Speed
472
in/min


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields