Crastin® HR5330HF NC010

Crastin® HR5330HF NC010

Manufacturer: DUPONT
Produced At: Import/ China
Product Category: PBT
Product No: Crastin HR5330HF NC010
Product Quantity: 25KG / BAG
Product Features: Hydrolysis Resistant


Crastin® HR5330HF NC010

THERMOPLASTIC POLYESTER RESIN
Product Description:
30% Glass Reinforced, Hydrolysis Resistant, Polybutylene Terephthalate
Filler / Reinforcement 

  • Glass Fiber, 30% Filler by Weight

Additive 

  • Mold Release

Features 

  • Hydrolysis Resistant

RoHS Compliance 

  • Contact Manufacturer

Forms 

  • Pellets

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Shear Modulus vs. Temperature, Dynamic (ISO 11403-1)

  • Shear Stress vs. Shear Rate (ISO 11403-1)

  • Specific Volume vs Temperature (ISO 11403-2)

  • Tensile Modulus vs. Temperature (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Part Marking Code (ISO 11469)

  • PBT-IGF30

Resin ID (ISO 1043)

  • PBT-IGF30

Physical
Nominal Value
Unit
Test Method
Density
1.50
g/cm³
ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)
0.519
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
1.0
%

Flow
0.30
%

Water Absorption


ISO 62
Saturation, 73°F, 0.0787 in
0.35
%

Equilibrium, 73°F, 0.0787 in, 50% RH
0.15
%

Viscosity Number
95.0
cm³/g
ISO 307
Flow Length 3 (78.7 mil)
14
in

Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.23E+6
psi
ISO 527-2
Tensile Stress (Break)
18100
psi
ISO 527-2
Tensile Strain (Break)
3.2
%
ISO 527-2
Flexural Modulus
1.09E+6
psi
ISO 178
Flexural Stress
29000
psi
ISO 178
Poisson's Ratio 4
0.34

ISO 527
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
5.5
ft·lb/in²

73°F
6.2
ft·lb/in²

Charpy Unnotched Impact Strength (73°F)
33
ft·lb/in²
ISO 179/1eU
Notched Izod Impact Strength


ISO 180/1A
-40°F
5.2
ft·lb/in²

73°F
6.7
ft·lb/in²

Unnotched Izod Impact Strength (73°F)
31
ft·lb/in²
ISO 180/1U
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
430
°F
ISO 75-2/B
264 psi, Unannealed
405
°F
ISO 75-2/A
Glass Transition Temperature 5
149
°F
ISO 11357-2
Vicat Softening Temperature
419
°F
ISO 306/B50
Melting Temperature 5
437
°F
ISO 11357-3
CLTE


ISO 11359-2
Flow
1.1E-5
in/in/°F

Flow : -40 to 73°F
1.4E-5
in/in/°F

Flow : 131 to 320°F
8.3E-6
in/in/°F

Transverse
8.3E-5
in/in/°F

Transverse : -40 to 73°F
5.0E-5
in/in/°F

Transverse : 131 to 320°F
8.1E-5
in/in/°F

Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
1.0E+13
ohms
IEC 60093
Volume Resistivity
> 1.0E+15
ohms·cm
IEC 60093
Electric Strength


IEC 60243-1
--
1100
V/mil

0.0394 in 6
790
V/mil

Relative Permittivity


IEC 60250
100 Hz
4.40


1 MHz
4.10


Dissipation Factor


IEC 60250
100 Hz
2.5E-3


1 MHz
0.020


Comparative Tracking Index
450
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Burning Rate 7 (0.0394 in)
1.2
in/min
ISO 3795
Flame Rating



0.030 in
HB

UL 94, IEC 60695-11-10, -20
0.06 in
HB

IEC 60695-11-10, -20
Oxygen Index
19
%
ISO 4589-2
FMVSS Flammability
B

FMVSS 302
Fill Analysis
Nominal Value
Unit

Melt Density
1.29
g/cm³

Ejection Temperature
338
°F

Specific Heat Capacity of Melt
0.413
Btu/lb/°F

Thermal Conductivity of Melt
1.9
Btu·in/hr/ft²/°F

Injection
Nominal Value
Unit

Drying Temperature
248
°F

Drying Time - Desiccant Dryer
2.0 to 4.0
hr

Suggested Max Moisture
0.040
%

Processing (Melt) Temp
464 to 500
°F

Melt Temperature, Optimum
482
°F

Mold Temperature
86 to 266
°F

Mold Temperature, Optimum
176
°F

Holding Pressure
8700
psi

Back Pressure
As low as possible


Drying Recommended
yes


Hold Pressure Time
3.00
s/mm