Products

CYCOLOY™ FR Resin CM6210

CYCOLOY™ FR Resin CM6210

Manufacturer: SABIC
Produced At:
 Import/ China
Product Category: Polycarbonate + ABS
Product No:
 CYCOLOY FR Resin CM6210
Product Quantity: 25KG / BAG
Product Features:
 Bromine FreeChlorine FreeFlame RetardantHigh Stiffness

CYCOLOY™ FR Resin CM6210

Polycarbonate + ABS
Product Description:
CYCOLOY CM6210 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a mineral filled, low warpage grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 flame rating. CYCOLOY CM6210 resin is an excellent candidate for a wide variety of applications including enclosures.

Additive 
  • Flame Retardant

Features 
  • Bromine Free,Chlorine Free,Flame Retardant,High Stiffness 
Uses 
  • Electrical/Electronic Applications

Processing Method 
  • Sheet Extrusion

Also Available In 
  • Asia PacificEurope 
Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity



--
1.28

ASTM D792
--
1.27
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)
12
g/10 min
ASTM D1238
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
0.549
in³/10min
ISO 1133
Molding Shrinkage - Flow (0.126 in)
4.0E-3 to 6.0E-3
in/in
Internal Method
Water Absorption


ISO 62
Saturation, 73°F
0.30
%

Equilibrium, 73°F, 50% RH
0.10
%

Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
98

ISO 2039-2
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus



-- 3
518000
psi
ASTM D638
--
531000
psi
ISO 527-2/1
Tensile Strength



Yield 4
9280
psi
ASTM D638
Yield
8560
psi
ISO 527-2/5
Yield
9140
psi
ISO 527-2/50
Break 4
7250
psi
ASTM D638
Break
9430
psi
ISO 527-2/5
Break
7250
psi
ISO 527-2/50
Tensile Elongation



Yield 4
4.9
%
ASTM D638
Yield
3.6
%
ISO 527-2/5
Yield
3.5
%
ISO 527-2/50
Break 4
80
%
ASTM D638
Break
100
%
ISO 527-2/5
Break
97
%
ISO 527-2/50
Flexural Modulus



1.97 in Span 5
508000
psi
ASTM D790
-- 6
516000
psi
ISO 178
Flexural Stress



-- 6, 7
15400
psi
ISO 178
Yield, 1.97 in Span 5
16000
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 8


ISO 179/1eA
-22°F
4.8
ft·lb/in²

73°F
21
ft·lb/in²

Notched Izod Impact



-22°F
1.7
ft·lb/in
ASTM D256
73°F
9.4
ft·lb/in
ASTM D256
-22°F 9
4.8
ft·lb/in²
ISO 180/1A
73°F 9
21
ft·lb/in²
ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
398
in·lb
ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed, 0.157 in, 3.94 in Span 10
210
°F
ISO 75-2/Be
264 psi, Unannealed, 0.126 in
194
°F
ASTM D648
264 psi, Unannealed, 0.157 in, 3.94 in Span 10
192
°F
ISO 75-2/Ae
Vicat Softening Temperature



--
223
°F
ASTM D1525 11
--
234
°F
ISO 306/B50
--
237
°F
ISO 306/B120
Ball Pressure Test


IEC 60695-10-2
163 to 171°F
Pass


203°F 12
Pass


CLTE



Flow : -40 to 104°F
3.2E-5
in/in/°F
ASTM E831
Flow : -40 to 104°F
2.9E-5
in/in/°F
ISO 11359-2
Flow : 73 to 140°F
2.9E-5
in/in/°F
ISO 11359-2
Transverse : -40 to 104°F
3.9E-5
in/in/°F
ASTM E831
Transverse : -40°F
3.3E-5
in/in/°F
ISO 11359-2
Transverse : 73 to 140°F
3.3E-5
in/in/°F
ISO 11359-2
Thermal Conductivity
2.1
Btu·in/hr/ft²/°F
ISO 8302
RTI Elec
140
°F
UL 746
RTI Imp
140
°F
UL 746
RTI Str
140
°F
UL 746
Electrical
Nominal Value
Unit
Test Method
Electric Strength


IEC 60243-1
0.0315 in, in Oil
970
V/mil

0.0630 in, in Oil
660
V/mil

0.126 in, in Oil
430
V/mil

Relative Permittivity


IEC 60250
50 Hz
2.90


60 Hz
2.90


1 MHz
2.80


Dissipation Factor


IEC 60250
50 Hz
3.0E-3


60 Hz
3.0E-3


1 MHz
4.0E-3


Comparative Tracking Index
250
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Flame Rating (0.06 in)
V-0

UL 94
Extrusion Notes
Sheet Extrusion Parameters
  • Drying Temperature: 80 to 90°C

  • Drying Time: 3 to 4 hrs

  • Drying Time (Cumulative): 12 hrs

  • Minimum Moisture Content: 0.04%

  • Melt Temperature: 220 to 245°C

  • Barrel - Zone 1 Temperature: 180 to 225°C

  • Barrel - Zone 2 Temperature: 190 to 230°C

  • Barrel - Zone 3 Temperature: 205 to 240°C

  • Barrel - Zone 4 Temperature: 210 to 245°C

  • Adapter Temperature: 210 to 245°C

  • Die Temperature: 210 to 245°C

  • Roll Stack Temperature - Top: 70 to 100°C

  • Roll Stack Temperature - Middle: 70 to 95°C

  • Roll Stack Temperature - Bottom: 65 to 90°C



Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields


Consultation