Radilon® CA RV300L 333 NER
Polyamide 66/6 Copolymer
PA66/6 copolymer injection moulding grade, 30% glass Fiber reinforced. Black colour.
Suitable for parts requiring high stiffness and good mechanical resistance. Good surface aspect and easier flow.
ISO 1043 : PA66/6 GF30
Filler / Reinforcement | |
Features | - Copolymer，Good Flow，Good Surface Finish，High Stiffness
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Multi-Point Data | |
Resin ID (ISO 1043) | |
Density | 1.28 | -- | g/cm³ | ISO 1183 |
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.0 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.7 | -- | % |
|
Tensile Modulus | 1.36E+6 | -- | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 23900 | -- | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 3.1 | -- | % | ISO 527-2/1A/5 |
Flexural Modulus 2 | 1.13E+6 | -- | psi | ISO 178 |
Flexural Stress 2 | 35500 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 3.8 | -- | ft·lb/in² |
|
73°F | 4.8 | -- | ft·lb/in² |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 33 | -- | ft·lb/in² |
|
73°F | 32 | -- | ft·lb/in² |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 455 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 419 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 437 | -- | °F | ISO 306/B50 |
Melting Temperature 3 | 473 | -- | °F | ISO 11357 |
Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index | 500 | -- | V | IEC 60112 |
Burning Rate | 0.0 | -- | in/min | FMVSS 302 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | < -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 518 to 554 | °F |
|
Mold Temperature | 176 to 194 | °F |
|
Injection Rate | Moderate-Fast |
|
|