Radilon® A RV500W 333 NER
Polyamide 66
PA66 50% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts requiring very high stiffness and mechanical resistance, along with excellent heat ageing properties retention.
Filler / Reinforcement | |
Additive | |
Features | - Heat Aging Resistant，Heat Stabilized，High Stiffness
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.58 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage 2 |
|
|
| ISO 294-4 |
Across Flow | 0.70 | -- | % |
|
Flow | 0.20 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 4.6 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
Tensile Modulus | 2.39E+6 | 2.10E+6 | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 34800 | 27600 | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 2.5 | 2.6 | % | ISO 527-2/1A/5 |
Flexural Modulus 3 | 2.22E+6 | -- | psi | ISO 178 |
Flexural Stress 3 | 50800 | -- | psi | ISO 178 |
Charpy Notched Impact Strength(73°F) | 5.7 | 8.1 | ft·lb/in² | ISO 179/1eA |
Charpy Unnotched Impact Strength(73°F) | 45 | 50 | ft·lb/in² | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
|
264 psi, Unannealed | 482 | -- | °F | ISO 75-2/Af |
1160 psi, Unannealed | 419 | -- | °F | ISO 75-2/Cf |
Vicat Softening Temperature | 482 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
Flammability | 0 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Mold Temperature | 176 to 212 | °F |
|
Injection Rate | Moderate-Fast |
|
|