Radilon® A 50W 100 M NAT 5770
Polyamide 66
PA66 very high viscosity extrusion grade. Heat stabilized. Natural colour.
Suitable for extrusion processes where very high impact resistance and excellent heat ageing properties are required. Also suitable for injection moulding of high thickness items.
ISO 1043 : PA66-T
Additive | |
Features | - Heat Aging Resistant，Heat Stabilized，High Impact Resistance，High Viscosity
|
RoHS Compliance | |
Appearance | |
Processing Method | - Extrusion，Injection Molding
|
Resin ID (ISO 1043) | |
Density | 1.14 | -- | g/cm³ | ISO 1183 |
Viscosity Number (H2SO4 (Sulphuric Acid)) | 295 | -- | cm³/g | ISO 307 |
Tensile Modulus | 450000 | -- | psi | ISO 527-2/1A/1 |
Tensile Stress (Yield) | 11600 | -- | psi | ISO 527-2/1A/50 |
Tensile Strain (Yield) | 4.0 | -- | % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 40 | -- | % | ISO 527-2/1A/50 |
Flexural Modulus 2 | 435000 | -- | psi | ISO 178 |
Flexural Stress 2 | 18100 | -- | psi | ISO 178 |
Charpy Notched Impact Strength(73°F) | 3.8 | -- | ft·lb/in² | ISO 179/1eA |
Heat Deflection Temperature (264 psi, Unannealed) | 185 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 464 | -- | °F | ISO 306/B50 |
Melting Temperature 3 | 500 | -- | °F | ISO 11357 |
Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Burning Rate | 0.0 | -- | in/min | FMVSS 302 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1380 | -- | °F | IEC 60695-2-12 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | < -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Mold Temperature | 158 to 194 | °F |
|
Injection Rate | Moderate |
|
|
Drying Temperature | 176 | °F |
|
Drying Time | 2.0 to 4.0 | hr |
|
Suggested Max Moisture | 0.15 | % |
|
Melt Temperature | 536 to 572 | °F |
|