Products

Stanyl® TW271F8

Stanyl® TW271F8

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TW271F8
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized、PTFE Lubricated、Platable

Stanyl® TW271F8

Polyamide 46
Product Description:
40% Glass Reinforced, Heat Stabilized, Wear and Friction Modified

Special Features:

  • Heat stabilized or stable to heat

  • Platable

  • Wear and friction modified


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 40% Filler by Weight

Additive 
  • Heat Stabilizer、PTFE Lubricant 
Features 
  • Heat Stabilized、Platable 
Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • (PA46+PTFE)-GF40

Physical
Nominal Value
Unit
Test Method
Density
1.63
g/cm³
ISO 1183
Viscosity Number
145
cm³/g
ISO 307
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.89E+6
psi
ISO 527-2
Tensile Stress (Break)
30500
psi
ISO 527-2
Tensile Strain (Break)
3.0
%
ISO 527-2
Flexural Modulus
1.67E+6
psi
ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (73°F)
6.7
ft·lb/in²
ISO 179/1eA
Notched Izod Impact Strength (73°F)
6.7
ft·lb/in²
ISO 180/1A
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
545
°F
ISO 75-2/B
264 psi, Unannealed
545
°F
ISO 75-2/A
Glass Transition Temperature 2
167
°F
ISO 11357-2
Vicat Softening Temperature
545
°F
ISO 306/B50
Melting Temperature 2
554
°F
ISO 11357-3
Injection
Nominal Value
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608
°F
Processing (Melt) Temp
581 to 608
°F
Mold Temperature
176 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
290 to 1450
psi
Screw Compression Ratio
2.5:1.0