Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TW271B6
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized、PTFE Lubricated

Stanyl® TW271B6

Polyamide 46
Product Description:
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified

Special Features:

  • Heat stabilized or stable to heat

  • Wear and friction modified


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Carbon Fiber, 30% Filler by Weight

Additive 
  • Heat Stabilizer、PTFE Lubricant 
Features 

  • Heat Stabilized

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • (PA46+PTFE)-CF30

Physical
Dry
Conditioned
Unit
Test Method
Density
1.32
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
0.70
--
%

Flow
0.30
--
%

Water Absorption



ISO 62
Saturation, 73°F
8.7
--
%

Equilibrium, 73°F, 50% RH
2.4
--
%

Viscosity Number
150
--
cm³/g
ISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus



ISO 527-2
--
3.48E+6
2.10E+6
psi

248°F
1.96E+6
--
psi

320°F
1.74E+6
--
psi

356°F
1.67E+6
--
psi

392°F
1.60E+6
--
psi

Tensile Stress



ISO 527-2
Break
37700
24700
psi

Break, 248°F
20300
--
psi

Break, 320°F
16700
--
psi

Break, 356°F
15200
--
psi

Break, 392°F
13800
--
psi

Tensile Strain



ISO 527-2
Break
1.7
3.5
%

Break, 248°F
3.1
--
%

Break, 320°F
3.1
--
%

Break, 356°F
3.1
--
%

Break, 392°F
3.1
--
%

Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
3.3
3.3
ft·lb/in²

73°F
3.3
8.1
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
24
26
ft·lb/in²

73°F
24
38
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
554
--
°F
ISO 75-2/A
Glass Transition Temperature 2
167
--
°F
ISO 11357-2
Melting Temperature 2
563
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.4E-5
--
in/in/°F

Transverse
1.9E-5
--
in/in/°F

Injection
Dry
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608
°F
Processing (Melt) Temp
581 to 608
°F
Mold Temperature
176 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
290 to 1450
psi
Screw Compression Ratio
2.5:1.0