Products

Stanyl® TW241F5

Stanyl® TW241F5

Manufacturer: Envalior/DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TW241F5
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized，Lubricated

Stanyl® TW241F5

Polyamide 46

Product Description:
Heat Stabilized, 25% Glass Reinforced, Lubricated

Special Features:

  • Contains release agent

  • Heat stabilized or stable to heat

  • Lubricated


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 25% Filler by Weight

Additive 

  • Heat Stabilizer、Lubricant、Mold Release

Features 

  • Heat Stabilized、Lubricated 

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PA46-GF25

Physical
Nominal Value
Unit
Test Method
Density
1.35
g/cm³
ISO 1183
Water Absorption


ISO 62
Saturation, 73°F
10
%

Equilibrium, 73°F, 50% RH
2.8
%

Viscosity Number
145
cm³/g
ISO 307
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
1.31E+6
psi
ISO 527-2
Tensile Stress (Break)
26100
psi
ISO 527-2
Tensile Strain (Break)
3.0
%
ISO 527-2
Flexural Modulus
1.09E+6
psi
ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (73°F)
3.8
ft·lb/in²
ISO 179/1eA
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
536
°F
ISO 75-2/A
Glass Transition Temperature 2
167
°F
ISO 11357-2
Melting Temperature 2
563
°F
ISO 11357-3
Injection
Nominal Value
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608
°F
Processing (Melt) Temp
581 to 608
°F
Mold Temperature
176 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
290 to 1450
psi
Screw Compression Ratio
2.5:1.0


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields