Stanyl® TS300

Stanyl® TS300

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TS300
Product Quantity: 25KG / BAG
Product Features: Lubricated

Stanyl® TS300

Polyamide 46
Product Description:
Special Features:

  • Contains release agent

  • Lubricated


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Additive 

  • Lubricant、Mold Release 

Features 

  • Lubricated

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PA46

Physical
Dry
Conditioned
Unit
Test Method
Density1.18--g/cm³ISO 1183
Molding Shrinkage


ISO 294-4
Across Flow2.0--%
Flow2.0--%
Water Absorption


ISO 62
Saturation, 73°F14--%
Equilibrium, 73°F, 50% RH3.7--%
Viscosity Number185--cm³/gISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus


ISO 527-2
--479000145000psi
248°F116000--psi
320°F94300--psi
356°F87000--psi
392°F72500--psi
Tensile Stress


ISO 527-2
Yield145007980psi
Yield, 248°F7250--psi
Yield, 320°F5800--psi
Yield, 356°F5080--psi
Yield, 392°F4350--psi
Tensile Strain (Yield)1020%ISO 527-2
Nominal Tensile Strain at Break


ISO 527-2
--40> 50%
356°F> 50--%
392°F> 50--%
Flexural Modulus


ISO 178
--435000131000psi
248°F116000--psi
320°F87000--psi
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F1.91.9ft·lb/in²
73°F4.817ft·lb/in²
Charpy Unnotched Impact Strength


ISO 179/1eU
-22°FNo BreakNo Break

73°FNo BreakNo Break

Notched Izod Impact Strength


ISO 180/1A
-40°F1.91.9ft·lb/in²
73°F4.817ft·lb/in²
Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed536--°FISO 75-2/B
264 psi, Unannealed374--°FISO 75-2/A
Glass Transition Temperature 2167--°FISO 11357-2
Vicat Softening Temperature554--°FISO 306/B50
Melting Temperature 2563--°FISO 11357-3
CLTE


ISO 11359-2
Flow4.7E-5--in/in/°F
Transverse6.1E-5--in/in/°F
InjectionDryUnit
Drying Temperature176°F
Drying Time4.0 to 8.0hr
Rear Temperature536 to 608°F
Middle Temperature572 to 608°F
Front Temperature572 to 608°F
Nozzle Temperature572 to 608°F
Processing (Melt) Temp590 to 608°F
Mold Temperature176 to 248°F
Injection RateModerate-Fast
Back Pressure290 to 1450psi
Screw Compression Ratio2.5:1.0