Products

Stanyl® TS200F10

Stanyl® TS200F10

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TS200F10
Product Quantity: 25KG / BAG
Product Features: Platable、Lubricated

Stanyl® TS200F10

Polyamide 46
Product Description:
50% Glass Reinforced

Special Features:

  • Contains release agent

  • Lubricated

  • Platable


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 50% Filler by Weight

Additive 

  • Lubricant、Mold Release 

Features 

  • Lubricated、Platable 

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PA46-GF50

Physical
Dry
Conditioned
Unit
Test Method
Density
1.62
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
0.90
--
%

Flow
0.40
--
%

Water Absorption



ISO 62
Saturation, 73°F
6.8
--
%

Equilibrium, 73°F, 50% RH
1.9
--
%

Viscosity Number
140
--
cm³/g
ISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus



ISO 527-2
--
2.32E+6
1.45E+6
psi

248°F
1.19E+6
--
psi

320°F
1.07E+6
--
psi

356°F
1.02E+6
--
psi

392°F
957000
--
psi

Tensile Stress



ISO 527-2
Break
36300
23200
psi

Break, 248°F
20300
--
psi

Break, 320°F
17400
--
psi

Break, 356°F
16000
--
psi

Break, 392°F
14500
--
psi

Tensile Strain



ISO 527-2
Break
2.7
5.0
%

Break, 248°F
5.0
--
%

Break, 320°F
5.0
--
%

Break, 356°F
5.0
--
%

Break, 392°F
5.0
--
%

Flexural Modulus



ISO 178
--
2.03E+6
1.31E+6
psi

248°F
1.06E+6
--
psi

320°F
943000
--
psi

Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
6.7
6.7
ft·lb/in²

73°F
7.6
11
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
43
48
ft·lb/in²

73°F
48
52
ft·lb/in²

Notched Izod Impact Strength



ISO 180/1A
-40°F
6.7
6.7
ft·lb/in²

73°F
7.6
11
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
554
--
°F
ISO 75-2/B
264 psi, Unannealed
554
--
°F
ISO 75-2/A
Glass Transition Temperature 3
167
--
°F
ISO 11357-2
Vicat Softening Temperature
554
--
°F
ISO 306/B50
Melting Temperature 3
563
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.4E-5
--
in/in/°F

Transverse
2.2E-5
--
in/in/°F

Effective Thermal Diffusivity
1.32E-7
--
m²/s



Injection
Dry
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608