Stanyl® TE250F9

Stanyl® TE250F9

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TE250F9
Product Quantity: 25KG / BAG
Product Features: Flame Retardant、Heat Stabilized、Lubricated、Platable

Stanyl® TE250F9

Polyamide 46
Product Description:
45% Glass Reinforced, Heat Stabilized, Flame Retardant

Special Features:

  • Contains release agent

  • Heat stabilized or stable to heat

  • Lubricated

  • Platable


Used In:

  • Reflow connectors


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 45% Filler by Weight

Additive 
  • Flame Retardant、Heat Stabilizer、Lubricant、Mold Release 
Features 
  • Flame Retardant、Heat Stabilized、Lubricated、Platable 
Uses 

  • Connectors

Processing Method 

  • Injection Molding

Multi-Point Data 

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Viscosity vs. Shear Rate (ISO 11403-2) 

Resin ID (ISO 1043)

  • PA46-GF45 FR(17)

Physical
Dry
Conditioned
Unit
Test Method
Density
1.82
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
0.90
--
%

Flow
0.30
--
%

Water Absorption



ISO 62
Saturation, 73°F
4.8
--
%

Equilibrium, 73°F, 50% RH
1.3
--
%

Viscosity Number
140
--
cm³/g
ISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus



ISO 527-2
--
2.47E+6
1.74E+6
psi

248°F
1.60E+6
--
psi

320°F
1.45E+6
--
psi

Tensile Stress



ISO 527-2
Break
29000
18900
psi

Break, 248°F
18900
--
psi

Break, 320°F
17400
--
psi

Tensile Strain



ISO 527-2
Break
2.0
3.0
%

Break, 248°F
3.0
--
%

Break, 320°F
3.0
--
%

Flexural Modulus



ISO 178
--
2.18E+6
1.60E+6
psi

248°F
1.52E+6
--
psi

320°F
1.31E+6
--
psi

Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
6.2
6.2
ft·lb/in²

73°F
6.2
7.1
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
24
24
ft·lb/in²

73°F
31
36
ft·lb/in²

Notched Izod Impact Strength



ISO 180/1A
-40°F
6.2
6.2
ft·lb/in²

73°F
6.2
7.1
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
554
--
°F
ISO 75-2/B
264 psi, Unannealed
554
--
°F
ISO 75-2/A
Glass Transition Temperature 3
167
--
°F
ISO 11357-2
Vicat Softening Temperature
554
--
°F
ISO 306/B50
Melting Temperature 3
563
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.1E-5
--
in/in/°F

Transverse
2.5E-5
--
in/in/°F

RTI Elec (0.030 in)
284
--
°F
UL 746
Effective Thermal Diffusivity
1.42E-7
--
m²/s

Thermal Index - 5000 hr
325
--
°F
IEC 60216
Injection
Dry
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608
°F
Processing (Melt) Temp
581 to 608
°F
Mold Temperature
176 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
290 to 1450
psi
Screw Compression Ratio
2.5:1.0