Products

Stanyl® TE200F8

Stanyl® TE200F8

Manufacturer: Envalior/DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TE200F8
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized，Platable

Stanyl® TE200F8

Polyamide 46

Product Description:
40% Glass Reinforced, Heat Stabilized, for E&E applications

Special Features:

  • Heat stabilized or stable to heat

  • Platable


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 40% Filler by Weight

Additive 

  • Heat Stabilizer

Features 

  • Heat Stabilized、Platable 

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PA46-GF40

Physical
Dry
Conditioned
Unit
Test Method
Density
1.51
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
1.1
--
%

Flow
0.50
--
%

Water Absorption



ISO 62
Saturation, 73°F
8.1
--
%

Equilibrium, 73°F, 50% RH
2.2
--
%

Viscosity Number
145
--
cm³/g
ISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus



ISO 527-2
--
1.89E+6
1.16E+6
psi

248°F
1.00E+6
--
psi

320°F
885000
--
psi

356°F
827000
--
psi

392°F
769000
--
psi

Tensile Stress



ISO 527-2
Break
33400
20300
psi

Break, 248°F
18900
--
psi

Break, 320°F
16700
--
psi

Break, 356°F
15200
--
psi

Break, 392°F
14500
--
psi

Tensile Strain



ISO 527-2
Break
3.0
6.0
%

Break, 248°F
6.5
--
%

Break, 320°F
6.5
--
%

Break, 356°F
6.5
--
%

Break, 392°F
6.5
--
%

Flexural Modulus



ISO 178
--
1.67E+6
1.02E+6
psi

248°F
841000
--
psi

320°F
754000
--
psi

Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
5.7
5.7
ft·lb/in²

73°F
6.7
10
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
36
40
ft·lb/in²

73°F
45
48
ft·lb/in²

Notched Izod Impact Strength



ISO 180/1A
-40°F
5.7
5.7
ft·lb/in²

73°F
6.7
10
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
554
--
°F
ISO 75-2/B
264 psi, Unannealed
554
--
°F
ISO 75-2/A
Glass Transition Temperature 2
167
--
°F
ISO 11357-2
Vicat Softening Temperature
554
--
°F
ISO 306/B50
Melting Temperature 2
563
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.4E-5
--
in/in/°F

Transverse
2.8E-5
--
in/in/°F

Effective Thermal Diffusivity
1.35E-7
--
m²/s

Thermal Index - 5000 hr
318
--
°F
IEC 60216
Injection
Dry
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 608
°F
Middle Temperature
572 to 608
°F
Front Temperature
572 to 608
°F
Nozzle Temperature
572 to 608
°F
Processing (Melt) Temp
581 to 608
°F
Mold Temperature
176 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
290 to 1450
psi
Screw Compression Ratio
2.5:1.0


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields