Products

Stanyl® 46SF5030

Stanyl® 46SF5030

Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl 46SF5030
Product Quantity: 25KG / BAG
Product Features: Good Flow、Heat Stabilized、Lubricated

Stanyl® 46HF4530

Polyamide 46
Product Description:
30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications

Special Features:

  • Contains release agent

  • Good or high flow

  • Heat stabilized or stable to heat

  • Lubricated


Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Filler / Reinforcement 

  • Glass Fiber, 30% Filler by Weight

Additive 

  • Heat Stabilizer、Lubricant、Mold Release

Features 

  • Good Flow、Heat Stabilized、Lubricated

Processing Method 

  • Injection Molding

Resin ID (ISO 1043)

  • PA46-GF30

Physical
Dry
Conditioned
Unit
Test Method
Density
1.41
--
g/cm³
ISO 1183
Molding Shrinkage



ISO 294-4
Across Flow
1.3
--
%

Flow
0.50
--
%

Water Absorption



ISO 62
Saturation, 73°F
9.5
--
%

Equilibrium, 73°F, 50% RH
2.6
--
%

Viscosity Number
95.0
--
cm³/g
ISO 307
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus



ISO 527-2
--
1.45E+6
870000
psi

248°F
798000
--
psi

320°F
725000
--
psi

356°F
682000
--
psi

392°F
653000
--
psi

Tensile Stress



ISO 527-2
Break
30500
16700
psi

Break, 248°F
18100
--
psi

Break, 320°F
16000
--
psi

Break, 356°F
13800
--
psi

Break, 392°F
13100
--
psi

Tensile Strain



ISO 527-2
Break
3.0
6.0
%

Break, 248°F
5.5
--
%

Break, 320°F
5.5
--
%

Break, 356°F
5.5
--
%

Break, 392°F
5.5
--
%

Flexural Modulus
1.31E+6
798000
psi
ISO 178
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength



ISO 179/1eA
-22°F
5.7
5.7
ft·lb/in²

73°F
6.2
8.1
ft·lb/in²

Charpy Unnotched Impact Strength



ISO 179/1eU
-22°F
29
29
ft·lb/in²

73°F
29
43
ft·lb/in²

Thermal
Dry
Conditioned
Unit
Test Method
Heat Deflection Temperature




66 psi, Unannealed
554
--
°F
ISO 75-2/B
264 psi, Unannealed
554
--
°F
ISO 75-2/A
Glass Transition Temperature 3
167
--
°F
ISO 11357-2
Vicat Softening Temperature
554
--
°F
ISO 306/B50
Melting Temperature 3
563
--
°F
ISO 11357-3
CLTE



ISO 11359-2
Flow
1.4E-5
--
in/in/°F

Transverse
3.3E-5
--
in/in/°F

RTI Elec (0.030 in)
149
--
°F
UL 746
Injection
Dry
Unit
Drying Temperature
176
°F
Drying Time
4.0 to 8.0
hr
Rear Temperature
536 to 590
°F
Middle Temperature
572 to 599
°F
Front Temperature
572 to 599
°F
Nozzle Temperature
572 to 590
°F
Processing (Melt) Temp
590 to 608
°F
Mold Temperature
140 to 248
°F
Injection Rate
Moderate-Fast

Back Pressure
145
psi
Screw Compression Ratio
2.5:1.0






Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields