Plexiglas® Satinice df33 7H
Polymethyl Methacrylate Acrylic
PLEXIGLAS® Satinice df33 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS® molding compound are
Extruded parts from PLEXIGLAS® Satinice df33 7H are characterized by the following special properties:
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
Additive | |
Features | |
Uses | - Automotive Applications，Construction Applications，Furniture，Lighting Diffusers，Profiles，Sheet
|
Appearance | |
Forms | |
Processing Method | |
Density | 1.18 | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.0549 | in³/10min | ISO 1133 |
Tensile Modulus | 479000 | psi | ISO 527-2/1 |
Tensile Stress (Break) | 9430 | psi | ISO 527-2/5 |
Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
Charpy Unnotched Impact Strength (73°F) | 8.1 | ft·lb/in² | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 214 | °F | ISO 75-2/B |
264 psi, Unannealed | 210 | °F | ISO 75-2/A |
Vicat Softening Temperature | 216 | °F | ISO 306/B50 |
CLTE - Flow (32 to 122°F) | 3.7E-5 | in/in/°F | ISO 11359-2 |
Glow Wire Ignition Temperature | 1290 | °F | IEC 60695-2-13 |
Gloss 2 |
|
| ISO 2813 |
105° | 16 |
|
|
90° | 9 |
|
|
Transmittance 3 | 69.0 | % | ISO 13468-2 |
Half-Value Angle | 34.0 | ° | DIN 5036 |
Scattering Power | 0.470 |
| DIN 5036 |
Drying Temperature | < 194 | °F |
|
Drying Time | 2.0 to 3.0 | hr |
|
Melt Temperature | 446 to 500 | °F |
|
Die Temperature | 446 to 500 | °F |
|