Product Features: Amorphous，High Clarity，High Impact Resistance，High Light Transmission，Impact Modified，Recyclable Material，Weather Resistant

Plexiglas® Resist AG 100

Polymethyl Methacrylate Acrylic
Evonik Industries AG
Product Description:

PLEXIGLAS® Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).

Properties
PLEXIGLAS® molding compounds have the following typical properties:

  • high weather resistance

  • excellent transmission and clarity

  • brilliant appearance

  • low weight - half the weight of glass

  • 100% recyclable - best life cycle assessment as compared with glass and PC

  • pleasant feel and sound of molded parts


PLEXIGLAS® Resist AG 100 is characterized by the following additional properties:

  • highest breaking strength and impact strength (30 times higher breaking strength than glass)

  • improved resistance to stress cracking

  • balanced property profile

  • clear reduction of reversible haze at very high and low temperatures

  • increased heat deflection temperature under load

  • AMECA listing, CAMPUS and moldflow data available


Additive 

  • Impact Modifier

Features 

  • Amorphous，High Clarity，High Impact Resistance，High Light Transmission，

  • Impact Modified，Recyclable Material，Weather Resistant

Uses 
  • Automotive Applications，Glazing 
Appearance 
  • Clear/Transparent，Transparent Green，Transparent Grey
Forms 

  • Pellets

Processing Method 
  • Coextrusion，Injection Molding，Sheet Extrusion
Physical
Nominal Value
Unit
Test Method
Density
1.16
g/cm³
ISO 1183
Melt Volume-Flow Rate (MVR)


ISO 1133
230°C/3.8 kg
0.0671
in³/10min

260°C/3.8 kg
0.470
in³/10min

Water Absorption


ISO 62
Saturation, 73°F
1.5
%

Equilibrium, 73°F, 50% RH
0.50
%

Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
319000
psi
ISO 527-2/1
Tensile Stress (Yield)
7980
psi
ISO 527-2/50
Tensile Strain (Yield)
5.0
%
ISO 527-2/50
Nominal Tensile Strain at Break
45
%
ISO 527-2
Impact
Nominal Value
Unit
Test Method
Charpy Unnotched Impact Strength (73°F)
57
ft·lb/in²
ISO 179/1eU
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
221
°F
ISO 75-2/B
264 psi, Unannealed
212
°F
ISO 75-2/A
Glass Transition Temperature
234
°F
ISO 11357-2
Vicat Softening Temperature
221
°F
ISO 306/B50
CLTE - Flow (32 to 122°F)
6.1E-5
in/in/°F
ISO 11359-2
Flammability
Nominal Value

Test Method
Flame Rating (0.06 in)
HB

IEC 707
Optical
Nominal Value
Unit
Test Method
Refractive Index
1.490

ISO 489
Transmittance 2
91.0
%
ISO 13468-2
Haze
0.70
%
ASTM D1003
Injection
Nominal Value
Unit

Drying Temperature
158 to 176
°F

Drying Time
3.0 to 4.0
hr

Processing (Melt) Temp
455 to 518
°F

Mold Temperature
140 to 176
°F

Extrusion
Nominal Value
Unit

Drying Temperature
158 to 176
°F

Drying Time
3.0 to 4.0
hr

Melt Temperature
455 to 518
°F

Die Temperature
464
°F


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields