Plexiglas® Hi-Gloss 8N black 9V022
Polymethyl Methacrylate Acrylic
PLEXIGLAS® Hi-Gloss 8N black 9V022 is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS® molding compounds are:
Special properties of PLEXIGLAS® Hi-Gloss 8N 9V022 are:
Application:
PLEXIGLAS® Hi-Gloss 8N black 9V022 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) black surfaces can be obtained.
Examples:
add-on automotive body parts
Features | |
Uses | - Automotive Applications，Automotive Exterior Parts
|
Appearance | |
Forms | |
Processing Method | |
Density | 1.19 | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.183 | in³/10min | ISO 1133 |
Tensile Modulus | 479000 | psi | ISO 527-2/1 |
Tensile Stress (Break) | 11200 | psi | ISO 527-2/5 |
Tensile Strain (Break) | 5.5 | % | ISO 527-2/5 |
Charpy Unnotched Impact Strength (73°F) | 9.5 | ft·lb/in² | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 217 | °F | ISO 75-2/B |
264 psi, Unannealed | 208 | °F | ISO 75-2/A |
Glass Transition Temperature | 243 | °F | ISO 11357-2 |
Vicat Softening Temperature | 226 | °F | ISO 306/B50 |
CLTE - Flow (32 to 122°F) | 4.4E-5 | in/in/°F | ISO 11359-2 |
Flammability Classification (0.06 in) | HB |
| IEC 60695-11-10, -20 |
Drying Temperature | < 208 | °F |
|
Drying Time | 2.0 to 3.0 | hr |
|
Processing (Melt) Temp | 428 to 500 | °F |
|
Mold Temperature | 140 to 194 | °F |
|