Makrolon® GF9002

Makrolon® GF9002

Manufacturer: Covestro
Produced At: Europe / China
Product Category: Polycarbonate（PC）
Product No: Makrolon GF9002 
Product Quantity: 25KG / BAG
Product Features: Good Mold Release，Low Viscosity，Flame Retardant

Makrolon® GF9002

Polycarbonate
Product Description:
MVR (300 °C/1.2 kg) 15 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.2 mm; low viscosity; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only; electrical/electronic; housing parts with low wall thickness
Filler / Reinforcement 

  • Glass Fiber, 10% Filler by Weight

Additive 

  • Flame Retardant

Features 
  • Flame Retardant，Good Mold Release，Low Viscosity
Uses 
  • Electrical/Electronic Applications，Housings，Thin-walled Parts
RoHS Compliance 

  • RoHS Compliant

Appearance 
  • Colors Available，Opaque 
Processing Method 

  • Injection Molding

Physical
Nominal Value
Unit
Test Method
Density (73°F)
1.27
g/cm³
ISO 1183
Apparent (Bulk) Density 3
0.64
g/cm³
ISO 60
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
17
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
0.915
in³/10min
ISO 1133
Molding Shrinkage 4


ISO 294-4
Across Flow : 0.0787 in
0.45
%

Flow : 0.0787 in
0.50
%

Water Absorption


ISO 62
Saturation, 73°F
0.30
%

Equilibrium, 73°F, 50% RH
0.10
%

Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus (73°F)
566000
psi
ISO 527-2/1
Tensile Stress


ISO 527-2/5
Yield, 73°F
8700
psi

Break, 73°F
6530
psi

Tensile Strain


ISO 527-2/5
Yield, 73°F
4.5
%

Break, 73°F
10
%

Flexural Modulus 5 (73°F)
537000
psi
ISO 178
Flexural Stress 5


ISO 178
73°F
15200
psi

3.5% Strain, 73°F
13100
psi

Flexural Strain at Flexural Strength 6 (73°F)
5.8
%
ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 7 (73°F, Complete Break)
3.8
ft·lb/in²
ISO 7391
Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F, Complete Break
> 19
ft·lb/in²

73°F, Complete Break
> 48
ft·lb/in²

Multi-Axial Instrumented Impact Energy (73°F)
11.8
ft·lb
ISO 6603-2
Multi-Axial Instrumented Impact Peak Force (73°F)
719
lbf
ISO 6603-2
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
270
°F
ISO 75-2/A
Vicat Softening Temperature



--
286
°F
ISO 306/B50
--
288
°F
ISO 306/B120
CLTE


ISO 11359-2
Flow : 73 to 131°F
2.2E-5
in/in/°F

Transverse : 73 to 131°F
3.3E-5
in/in/°F

RTI Elec (0.030 in)
176
°F
UL 746
RTI Imp (0.030 in)
176
°F
UL 746
RTI Str (0.030 in)
176
°F
UL 746
Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
1.0E+16
ohms
IEC 60093
Volume Resistivity (73°F)
1.0E+16
ohms·cm
IEC 60093
Electric Strength (73°F, 0.0394 in)
910
V/mil
IEC 60243-1
Relative Permittivity


IEC 60250
73°F, 100 Hz
3.20


73°F, 1 MHz
3.20


Dissipation Factor


IEC 60250
73°F, 100 Hz
1.0E-3


73°F, 1 MHz
9.0E-3


Comparative Tracking Index


IEC 60112
Solution A
175
V

Solution B
125
V

Flammability
Nominal Value
Unit
Test Method
Flame Rating


UL 94
0.030 in
V-1


0.05 in
V-0


Glow Wire Flammability Index


IEC 60695-2-12
0.030 in
1760
°F

0.06 in
1760
°F

0.12 in
1760
°F

Glow Wire Ignition Temperature


IEC 60695-2-13
0.06 in
1470
°F

0.12 in
1610
°F

Oxygen Index 8
37
%
ISO 4589-2
Burning Rate - US-FMVSS (> 39.4 mil)
passed

ISO 3795
Additional Information
Nominal Value


ISO Shortname
ISO 7391-PC,MFR,(,,)-18-9,GF10



Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields