Products

Makrolon® 6267 X

Makrolon® 6267 X

Manufacturer: Covestro
Produced At: Europe / China
Product Category: Polycarbonate（PC）
Product No: Makrolon 6267 X 
Product Quantity: 25KG / BAG
Product Features: Good Mold Release，Low Viscosity，Flame Retardant

Makrolon® 6267 X

Polycarbonate
Product Description:
MVR (300 °C/1.2 kg) 19 cm³/10 min; flame retardant; UL 94V-0/1.5 mm; low viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; available in opaque colors only
Additive 
  • Flame Retardant，UV Stabilizer 
Features 
  • Flame Retardant，Good Mold Release，Low Viscosity
RoHS Compliance 

  • RoHS Compliant

Appearance 
  • Colors Available，Opaque 
Processing Method 

  • Injection Molding

Physical
Nominal Value
Unit
Test Method
Density (73°F)
1.20
g/cm³
ISO 1183
Apparent (Bulk) Density 3
0.64
g/cm³
ISO 60
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
20
g/10 min
ISO 1133
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
1.16
in³/10min
ISO 1133
Molding Shrinkage



Across Flow
0.50 to 0.70
%
ISO 2577
Flow
0.50 to 0.70
%
ISO 2577
Across Flow : 0.0787 in 4
0.65
%
ISO 294-4
Flow : 0.0787 in 4
0.65
%
ISO 294-4
Water Absorption


ISO 62
Saturation, 73°F
0.30
%

Equilibrium, 73°F, 50% RH
0.12
%

Hardness
Nominal Value
Unit
Test Method
Ball Indentation Hardness
16800
psi
ISO 2039-1
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus (73°F)
355000
psi
ISO 527-2/1
Tensile Stress


ISO 527-2/50
Yield, 73°F
9720
psi

Break, 73°F
9430
psi

Tensile Strain


ISO 527-2/50
Yield, 73°F
6.0
%

Break, 73°F
120
%

Nominal Tensile Strain at Break (73°F)
> 50
%
ISO 527-2/50
Flexural Modulus 5 (73°F)
348000
psi
ISO 178
Flexural Stress 5


ISO 178
73°F
14100
psi

3.5% Strain, 73°F
10700
psi

Flexural Strain at Flexural Strength 6 (73°F)
6.9
%
ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 7


ISO 7391
-22°F, Complete Break
5.7
ft·lb/in²

73°F, Partial Break
29
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
No Break


73°F
No Break


Notched Izod Impact Strength 8


ISO 7391
-22°F, Complete Break
5.2
ft·lb/in²

73°F, Partial Break
7.1
ft·lb/in²

Multi-Axial Instrumented Impact Energy


ISO 6603-2
-22°F
40.6
ft·lb

73°F
36.9
ft·lb

Multi-Axial Instrumented Impact Peak Force


ISO 6603-2
-22°F
1330
lbf

73°F
1120
lbf

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature



66 psi, Unannealed
273
°F
ISO 75-2/B
264 psi, Unannealed
252
°F
ISO 75-2/A
Vicat Softening Temperature



--
291
°F
ISO 306/B50
--
293
°F
ISO 306/B120
Ball Pressure Test (275°F)
Pass

IEC 60695-10-2
CLTE


ISO 11359-2
Flow : 73 to 131°F
3.6E-5
in/in/°F

Transverse : 73 to 131°F
3.6E-5
in/in/°F

Thermal Conductivity 9 (73°F)
1.4
Btu·in/hr/ft²/°F
ISO 8302
RTI Elec (0.06 in)
257
°F
UL 746
RTI Imp (0.06 in)
239
°F
UL 746
RTI Str (0.06 in)
257
°F
UL 746
Flammability
Nominal Value
Unit
Test Method
Flame Rating (0.06 in)
V-0

UL 94
Glow Wire Flammability Index


IEC 60695-2-12
0.030 in
1760
°F

0.06 in
1760
°F

0.12 in
1760
°F

Oxygen Index 10
36
%
ISO 4589-2
Application of Flame from Small Burner - Method K and F (78.7 mil)
K1, F1

DIN 53438-1, -3
Burning Rate - US-FMVSS (> 39.4 mil)
passed

ISO 3795
Flash Ignition Temperature
860
°F
ASTM D1929
Needle Flame Test


IEC 60695-11-5
Method F : 59.1 mil
2.0
min

Method F : 78.7 mil
2.0
min

Method F : 0.12 in
2.0
min

Method K : 59.1 mil
2.0
min

Method K : 78.7 mil
2.0
min

Method K : 0.12 in
2.0
min

Self Ignition Temperature
986
°F
ASTM D1929


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields