Ultradur® S 4090 G2
Polybutylene Terephthalate + ASA
Product Description:
Low-warpage, easy-flowing injection molding grade with 10% glass fibres for technical parts, for which dimensional stability is very important (eg, housings, plug-and-socket connectors).
Filler / Reinforcement | Glass Fiber, 10% Filler by Weight
|
Uses | Connectors、Engineering PartsHousings |
Agency Ratings | |
RoHS Compliance | |
Appearance | |
Forms | |
Processing Method | |
Multi-Point Data | Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Viscosity vs. Shear Rate (ISO 11403-2) |
Resin ID (ISO 1043) | |
Density | 1.31 | g/cm³ | ISO 1183 |
Apparent (Bulk) Density | 0.70 to 0.80 | g/cm³ |
|
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 1.22 | in³/10min | ISO 1133 |
Water Absorption |
|
| ISO 62 |
Saturation, 73°F | 0.40 | % |
|
Equilibrium, 73°F, 50% RH | 0.20 | % |
|
Viscosity Number 3 | 105 | cm³/g | ISO 307 |
Mold Shrinkage 4 |
|
|
|
free, longitudinal | 0.46 | % |
|
free, transverse | 0.85 | % |
|
Ball Indentation Hardness (H 961/30) | 20300 | psi | ISO 2039-1 |
Tensile Modulus | 653000 | psi | ISO 527-2 |
Tensile Stress (Break) | 10900 | psi | ISO 527-2 |
Tensile Strain (Break) | 2.9 | % | ISO 527-2 |
Tensile Creep Modulus 5 (1000 hr) | 479000 | psi | ISO 899-1 |
Flexural Modulus | 595000 | psi | ISO 178 |
Flexural Stress | 17300 | psi | ISO 178 |
Charpy Notched Impact Strength |
|
| ISO 179/1eA |
-22°F | 1.5 | ft·lb/in² |
|
73°F | 1.9 | ft·lb/in² |
|
Charpy Unnotched Impact Strength |
|
| ISO 179/1eU |
-22°F | 11 | ft·lb/in² |
|
73°F | 18 | ft·lb/in² |
|
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 374 | °F | ISO 75-2/B |
264 psi, Unannealed | 221 | °F | ISO 75-2/A |
Melting Temperature | 433 | °F | ISO 11357-3 |
CLTE - Flow (73 to 176°F) | 3.1E-5 | in/in/°F | ISO 11359-2 |
Specific Heat | 0.287 | Btu/lb/°F |
|
Thermal Conductivity | 1.9 | Btu·in/hr/ft²/°F | DIN 52612 |
Maximum Service Temperature - short cycle operation | 338 | °F |
|
Temperature Index - at 50% loss of tensile strength |
|
| IEC 60216 |
-- 6 | 230 | °F |
|
-- 7 | 284 | °F |
|
Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
Relative Permittivity |
|
| IEC 60250 |
100 Hz | 3.60 |
|
|
1 MHz | 3.40 |
|
|
Dissipation Factor |
|
| IEC 60250 |
100 Hz | 3.1E-3 |
|
|
1 MHz | 0.021 |
|
|
Comparative Tracking Index |
|
| IEC 60112 |
Solution A | 375 | V |
|
Solution B | 125 | V |
|
Flammability Classification |
|
| IEC 60695-11-10, -20 |
0.030 in | HB |
|
|
0.06 in | HB |
|
|
Drying Temperature | 176 to 248 | °F |
|
Drying Time | 4.0 | hr |
|
Suggested Max Moisture | 0.040 | % |
|
Hopper Temperature | 176 | °F |
|
Rear Temperature | 500 | °F |
|
Middle Temperature | 509 | °F |
|
Front Temperature | 518 | °F |
|
Nozzle Temperature | 518 | °F |
|
Processing (Melt) Temp | 482 to 527 | °F |
|
Mold Temperature | 140 to 212 | °F |
|
Screw Speed | < 591 | in/min |
|