Ultraform® H 2320 006

Ultraform® H 2320 006

Manufacturer:  BASF
Produced At:  Europe / China
Product Category:  Acetal (POM) Copolymer
Product No:  Ultraform H2320 006
Product Quantity:  25KG / BAG
Product Features:  High Molecular Weight

Ultraform® H 2320 006

Acetal (POM) Copolymer
Product Description:
High-molecular-weight grade with somewhat increased flowability for injection molding of relatively thick-walled moldings.
Features 

  • High Molecular Weight

Uses 

  • Thick-walled Parts

Agency Ratings 

  • EC 1907/2006 (REACH)

RoHS Compliance 

  • RoHS Compliant

Forms 

  • Granules

Processing Method 
  • ExtrusionInjection Molding 
Multi-Point Data 

  • Isochronous Stress vs. Strain (ISO 11403-1)

  • Isothermal Stress vs. Strain (ISO 11403-1)

  • Secant Modulus vs. Strain (ISO 11403-1)

  • Shear Modulus vs. Temperature (ISO 11403-1)

  • Specific Heat vs. Temperature (ISO 11403-2)

  • Specific Volume vs Temperature (ISO 11403-2)

  • Viscosity vs. Shear Rate (ISO 11403-2)

Resin ID (ISO 1043)

  • POM

Physical
Nominal Value
Unit
Test Method
Density
1.40
g/cm³
ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
0.177
in³/10min
ISO 1133
Molding Shrinkage


ISO 294-4
Across Flow
2.1
%

Flow
2.1
%

Water Absorption


ISO 62
Saturation, 73°F
0.80
%

Equilibrium, 73°F, 50% RH
0.20
%

Hardness
Nominal Value
Unit
Test Method
Ball Indentation Hardness (H 358/30)
19600
psi
ISO 2039-1
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
377000
psi
ISO 527-2
Tensile Stress (Yield)
9280
psi
ISO 527-2/50
Tensile Strain (Yield)
11
%
ISO 527-2/50
Nominal Tensile Strain at Break
30
%
ISO 527-2/50
Tensile Creep Modulus 3 (1000 hr)
189000
psi
ISO 899-1
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength


ISO 179/1eA
-22°F
2.6
ft·lb/in²

73°F
2.9
ft·lb/in²

Charpy Unnotched Impact Strength


ISO 179/1eU
-22°F
95
ft·lb/in²

73°F
120
ft·lb/in²

Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature (264 psi, Unannealed)
203
°F
ISO 75-2/A
Melting Temperature
331
°F
ISO 11357-3
CLTE - Flow (73 to 131°F)
6.7E-5
in/in/°F
ISO 11359-2
Maximum Service Temperature - short cycle operation
212
°F

Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
1.0E+13
ohms
IEC 60093
Volume Resistivity
1.0E+15
ohms·cm
IEC 60093
Relative Permittivity (1 MHz)
3.80

IEC 60250
Dissipation Factor (1 MHz)
5.0E-3

IEC 60250
Comparative Tracking Index (Solution A)
600
V
IEC 60112
Flammability
Nominal Value
Unit
Test Method
Flammability Classification (0.06 in)
HB

IEC 60695-11-10, -20
Additional Information
Nominal Value

Test Method
ISO Type
POM-K, M-GNR, 01-002

ISO 9988-1
Injection
Nominal Value
Unit

Drying Temperature
212
°F

Drying Time
3.0
hr

Suggested Max Moisture
0.20
%

Hopper Temperature
392
°F

Rear Temperature
392
°F

Middle Temperature
392
°F

Front Temperature
392
°F

Nozzle Temperature
392
°F

Processing (Melt) Temp
374 to 446
°F

Mold Temperature
140 to 248
°F

Residence Time
< 10.0
min

Screw Speed
< 709
in/min


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields


Consultation

Shanghai Langqi Plastic Materials Co., Ltd.   沪ICP备12022668号 公安机关备案号：31011202003696