Shanghai Langqi Plastic Materials Co., Ltd.

Ultramid® A3Z

Manufacturer: BASF
Produced At: Europe / China
Product Category: Polyamide 66 Copolymer
Product No: Ultramid A3Z
Product Quantity: 25KG / BAG
Product Features: Impact Modified、Low Temperature Impact Resistance、Oil Resistant

Product information

Ultramid® A3Z

Polyamide 66

BASF Corporation

Product Description:

An impact-modified and stabilized injection moulding grade for components and housings with good low temperature impact resistance.

Additive	Impact Modifier
Features	Impact Modified、Low Temperature Impact Resistance、Oil Resistant
Uses	Housings
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.06	--	g/cm³	ISO 1183
Apparent (Bulk) Density	0.70	--	g/cm³
Melt Volume-Flow Rate (MVR)(275°C/10.0 kg)	1.28	--	in³/10min	ISO 1133
Water Absorption				ISO 62
Saturation, 73°F	6.7 to 7.7	--	%
Equilibrium, 73°F, 50% RH	2.0 to 2.6	--	%
Mold Shrinkage - constrained 3	0.85	--	%

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	276000	123000	psi	ISO 527-2
Tensile Stress (Yield)	6960	5800	psi	ISO 527-2/50
Tensile Strain (Yield)	5.0	18	%	ISO 527-2/50
Nominal Tensile Strain at Break	45	> 50	%	ISO 527-2/50
Tensile Creep Modulus 4 (1000 hr)	--	65300	psi	ISO 899-1
Flexural Modulus	254000	--	psi	ISO 178
Flexural Stress	9280	--	psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-22°F	15	--	ft·lb/in²
73°F	43 ft·lb/in²	No Break
Charpy Unnotched Impact Strength(73°F)	No Break	No Break		ISO 179/1eU
Notched Izod Impact Strength				ISO 180/A
-22°F	14	24	ft·lb/in²
73°F	43 ft·lb/in²	No Break

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	257	--	°F	ISO 75-2/B
264 psi, Unannealed	140	--	°F	ISO 75-2/A
Melting Temperature	500	--	°F	ISO 11357-3
CLTE - Flow (73 to 176°F)	3.9E-5 to 5.6E-5	--	in/in/°F	ISO 11359-2
Specific Heat	0.406	--	Btu/lb/°F
Thermal Conductivity	2.3	--	Btu·in/hr/ft²/°F	DIN 52612

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+12	ohms	IEC 60093
Volume Resistivity	4.0E+14	1.0E+12	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.10	3.60		IEC 60250
Dissipation Factor (1 MHz)	0.016	0.070		IEC 60250
Comparative Tracking Index(Solution A)	600	--	V	IEC 60112
Flammability	Dry	Conditioned	Unit	Test Method
Flammability Classification (0.06 in)	HB	--		IEC 60695-11-10, -20

Additional Information	Dry	Conditioned
Polymer Abbreviation	PA66-I	--

Injection	Dry	Unit
Drying Temperature	176	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.15	%
Hopper Temperature	176	°F
Rear Temperature	554	°F
Middle Temperature	554	°F
Front Temperature	554	°F
Nozzle Temperature	554	°F
Processing (Melt) Temp	536 to 572	°F
Mold Temperature	140 to 176	°F
Residence Time	< 10.0	min
Screw Speed	< 709	in/min