Shanghai Langqi Plastic Materials Co., Ltd.

Ultramid® A3WG10

Manufacturer: BASF
Produced At: Europe / China
Product Category: Polyamide 66 Copolymer
Product No: Ultramid A3WG10
Product Quantity: 25KG / BAG
Product Features: High Stiffness、Heat Aging Resistant、Oil Resistant

Product information

Ultramid® A3WG10

Polyamide 66

BASF Corporation

Product Description:

Ultramid A3WG10 is a 50% glass fiber reinforced and heat aging resistance injection molding PA66 grade.

Applications
Typical applications include industrial articles having very high rigidity.

Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Features	Heat Aging Resistant、High Rigidity、Oil Resistant
Uses	Industrial Applications
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density / Specific Gravity
--	1.55	--		ASTM D792
--	1.55	--	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg)	1.22	--	in³/10min	ISO 1133
Molding Shrinkage - Flow (0.125 in)	1.0E-3	--	in/in
Water Absorption
Saturation	4.0	--	%	ASTM D570
Saturation, 73°F	4.0	--	%	ISO 62
Equilibrium, 50% RH	1.2	--	%	ASTM D570
Equilibrium, 73°F, 50% RH	1.2	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (73°F)	2.44E+6	1.81E+6	psi	ISO 527-2
Tensile Strength
Break, 73°F	33400	--	psi	ASTM D638
Break, 73°F	33400	26100	psi	ISO 527-2
Break, 176°F	21900	16400	psi	ISO 527-2
Tensile Elongation
Break, 73°F	2.0	--	%	ASTM D638
Break, 73°F	2.5	3.5	%	ISO 527-2
Break, 176°F	5.2	4.9	%	ISO 527-2
Flexural Modulus
73°F	1.70E+6	--	psi	ASTM D790
73°F	2.18E+6	--	psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179
-22°F	6.2	--	ft·lb/in²
73°F	8.6	12	ft·lb/in²
Charpy Unnotched Impact Strength				ISO 179
-22°F	40	--	ft·lb/in²
73°F	45	48	ft·lb/in²
Notched Izod Impact				ASTM D256
-40°F	1.9	--	ft·lb/in
73°F	2.5	--	ft·lb/in

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed	482	--	°F	ASTM D648, ISO 75-2/B
264 psi, Unannealed	482	--	°F	ASTM D648, ISO 75-2/A
Peak Melting Temperature	500	--	°F	ASTM D3418, ISO 3146
CLTE
Flow	3.9E-6	--	in/in/°F	ASTM E831
Flow	7.2E-6	--	in/in/°F
Transverse	3.1E-5	--	in/in/°F
RTI Elec				UL 746
0.031 in	257	--	°F
0.06 in	257	--	°F
0.12 in	257	--	°F
RTI Imp				UL 746
0.06 in	266	--	°F
0.12 in	266	--	°F
RTI Str				UL 746
0.06 in	266	--	°F
0.12 in	266	--	°F

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity
0.0591 in	1.0E+15	1.0E+12	ohms·cm	ASTM D257
--	1.0E+15	1.0E+12	ohms·cm	IEC 60093
Dielectric Constant (1 MHz)	3.80	6.60		IEC 60250
Dissipation Factor				IEC 60250
100 Hz	0.015	0.17
1 MHz	0.015	0.30
Comparative Tracking Index	450	450	V	IEC 60112
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.031 in	HB	--
0.06 in	HB	--
0.12 in	HB	--

Injection	Dry	Unit
Drying Temperature	176	°F
Drying Time	2.0 to 4.0	hr
Suggested Max Moisture	0.15	%
Processing (Melt) Temp	536 to 581	°F
Mold Temperature	176 to 194	°F
Injection Pressure	500 to 1500	psi
Injection Rate	Fast